High Temperature Inorganic Glue for Ceramic and Aluminosilicate
Basic Info
| Model NO. | YN-049 |
| CAS No. | No |
| Formula | No |
| EINECS | No |
| Bonding Function | High Temperature Resistant Adhesive |
| Morphology | Solid and Solvent |
| Application | Fiber & Garment, Ceramic |
| Material | Epoxy |
| Classification | Room Curing |
| Main Agent Composition | Inorganic Adhesive Material |
| Characteristic | Weatherability |
| Promoter Composition | Stabilizer |
| Composition | Inorganic Material |
| Color | Grey |
| Temperature | 1400c, 1700, 900c |
| Usage | Ceramic Glue |
| Type | C-2, C-3, Cps |
| Transport Package | Plywood Case |
| Specification | CUSTOMIZED |
| Trademark | Yunnuo |
| Origin | China |
| HS Code | 8547100000 |
Product Description
Property of condensate | C-2 | C-3 | CPS cupric oxide |
Color | gray | gray | black |
Heat resistant temperature C | 1730 | 1460 | 980 |
Hardness | Hard,brittle | Hard,brittle | Hard,brittle |
Electrical properties | Good insulation performance at high temperature | Good insulation performance at high temperature | Good insulation at room temperature |
Medium resistance | Oil resistant, acid and alkali resistant, not resistant to boiling water | Oil resistant, acid and alkali resistant, not resistant to boiling water | Oil resistant, acid and alkali resistant, not resistant to boiling water |
Coefficient of linear expansion | Similar to ceramic(80×10-6/C) | Similar to steel(12.9×10-6/C) | Close to steel, |
Socket strength / tensile strength (steel-steel)Mpa | 82/37 | 79/34 | 96/- |
Applied range | High-temperature instrumentation, electronics, temperature-measuring element coating and potting, high-temperature anti-oxidation | Bonding and potting of high temperature resistant metal parts, high temperature oxidation resistant coating of metal materials, | Metal sleeve sticking, |
Proportion of glue solid phase | 1.6-2.5g | 1.6-2.5g | 3.5-5.5g |
Proportion of glue liquid phase | 1ml(about 1.39g) | 1ml(about 1.39g) | 1ml (about 1.7g) |
Curing procedures | Room temperature 12-24 hours → 80C 2 hours → 150C 2 hours, cool slowly | Room temperature 12-24 hours → 80C 2 hours → 150C 2 hours, cool slowly | Slow heating,→ 80C 2 hours → 150C 2 hours, cool slowly |
Net weight | 500g | 500g | 750g |
HT-CPS high temperature structural adhesivePhysical state: powder + liquidOperating time: 30minCuring conditions: 1. room temperature 12h; 2.80 C 2h; 3.150 C 2hColour: BlackDensity (g/cm3): 3.5Shear strength (MPa) GB / T7124-1999: 86 (socket)Impact strength (J / cm2) GB / T6328-1986: 8Tensile strength (MPa) GB / T6329-1996: 38.5Peel strength (N / cm) GB / T2791-1981: ---Working temperature (C): -196 ~ 980Heat-resistant temperature: 980 ºCWeight: 750g per groupMaterial: Inorganic copper oxide, temperature resistance 980 ºC.Uses: Used for bonding various hard alloy and ceramic turning tools, milling cutters, drills or gear cutters. The socket strengthis extremely high, which can be used to make extension rods and repair defects in high temperature casting conditions.Use operation1. Roughen the bonding surface and remove rust, oil and grease. The joint design is best with socket.2. Glue adjustment: The solid and liquid phases of various types of glue are adjusted according to the ratio of the technical index table, and it should be adjusted to a uniform and flowable paste. CPS copper oxide inorganic glue should not be excessively adjusted each time. It is best to adjust the glue on the containers (such as copper) that dissipate quickly.3. Curing with glueApply (fill) the glue to the surface to be bonded (sealed), and apply a little contact pressure to cure it after assembly. If thestrength is not high and medium resistance is not required, it can be cured at room temperature. Otherwise, please follow the curing procedure of the technical specification table.
Product name: HT C-2 ultra high temperature repair agentPhysical state: solid+liquidOperating time: 30minCuring conditions: 1.) Room temperature 12h; 2.) 80C -150C 2h; 3.) Slow coolingColor: off-whiteDensity (g /cm3): 1.4Compressive strength (MPa) GB / T1041-1992: 82 (socket strength)Shear strength (MPa) GB / T7124-1999: 37 (tensile strength)Bending strength (MPa) GB / T1024-1992:-Insulation strength (kv / mm) GB / T2411-1980: 30Working temperature (C): -60 ~ 1730Net weight: 500g two-componentUses: Inorganic ceramic material, temperature resistance 1730 C. It can repair equipment working under high temperatureconditions, such as repairing damaged or broken acid resistant tanks, blast furnace lining, steel ingot molds and other equipment,burner ignition devices, potting of molten steel temperature probes, etc.