Interfacial properties of SiCf/SiC minicomposites with a scheelite coating

Oct 26, 2023

Scientific Reports volume 12, Article number: 21950 (2022) Cite this article

666 Accesses

Metrics details

Unidirectional SiCf/SiC minicomposite with a scheelite (CaWO4) interphase coating was fabricated through the precursor infiltration and pyrolysis method. Fractography of the SiCf/SiC minicomposites indicated that weak fiber/matrix bonding can be provided by the CaWO4 interphase. Furthermore, interfacial debonding stress of SiCf/CaWO4/SiC minicomposite was evaluated through the fiber push-out test, and estimated to be 80.7 ± 4.6 MPa. In-situ tensile SEM observation of SiCf/CaWO4/SiC minicomposite after oxidation at 1000–1100 °C was carried out, and thermal compatibility between CaWO4 interphase coating and SiC fiber or matrix after heat treatment at 1300 °C was investigated.

Incorporation of reinforcing fibers into a brittle ceramic matrix provides a degree of pseudo-ductility to ceramic matrix composites (CMCs), typically the SiC fiber-reinforced SiC matrix composite (SiCf/SiC), preventing catastrophic failure by several mechanisms, such as fiber debonding, fiber sliding and crack bridging. SiCf/SiC composites are considered to be promising materials durable for severe environment applications such as super-sonic transport, space planes and fusion reactors1,2,3. The deviation of matrix cracks within the fiber-matrix interphase zone is realized and controlled by the deposition of a coating layer of a compliant material on the fibers prior to matrix fabrication4,5,6. The most effective interphase coating is considered to be PyC or BN coating7,8,9. However, the application of SiCf/SiC composites is limited by degradation of mechanical properties in oxidizing environments, due to oxidation of the PyC or BN coating at the fiber/matrix interface, particularly at intermediate temperatures4, 10.

Alternative oxidation-resistant interphase materials such as rare-earth orthophosphate monazite (LaPO4) have been considered as oxidation-resistant fiber-matrix interphases for CMCs due to the layered crystal structure and plastic deformation possibility. Studies on the LaPO4 interphase showed that it could be deformed under mechanical stresses at low temperatures by twinning and dislocation11,12,13. However, it was found to be thermodynamically incompatible with SiC14, 15. Both compatibility and oxidation resistance are important for the interphase coating to ensure the long period application of CMCs in air. Shanmugham et al. showed that a mullite interphase in SiCf/SiC composites deflected cracks even after exposure in air at 1000 °C for 24 h16. Lee et al. demonstrated the use of multilayer SiO2/ZrO2/SiO2 oxide coatings for SiC/SiC composites. Composite strength and crack deflection were retained after oxidation in air at 960 °C for 10 h17. Scheelite (CaWO4) has a layered structure consisting of (WO4) tetrahedra and eight-coordinated Ca sites and cleavage of its crystal was reported on (101) planes. The layered crystal structure and plastic deformation possibility of scheelite (CaWO4) make it another potential interphase material for SiCf/SiC composites18,19,20,21,22. So far, the fabrication of scheelite materials as the interphase coating in SiCf/SiC composite and the investigation on its effect has not been explored.

In this work, unidirectional SiCf/CaWO4/SiC minicomposite was prepared through the precursor infiltration and pyrolysis (PIP) method. The effectiveness of the CaWO4 interphase coating was investigated by comparing the fractography of SiCf/SiC composites with and without CaWO4 interphase coating. The interfacial property of the composites was quantitatively characterized by fiber push-out tests. The SiCf/CaWO4/SiC composites were oxidized at 1000–1100 °C to evaluate the oxidation resistance of the CaWO4 interphase coating in oxygen-rich environments. In addition, SiCf/CaWO4/SiC composites were heat-treated at 1300 °C to investigate the compatibility between CaWO4 interphase coating and SiC fiber or matrix.

Continuous CaWO4 interphase coatings were prepared on KD-II SiC fiber (provided by NUDT, China) through the sol–gel method. The property of the fiber can be found in the reference23. The detailed coating process was described in our previous work19, 20. The optimized firing temperature of 900℃ and atmosphere in Ar were used to avoid the fiber strength degradation during the coating process. The suitable coating thickness was obtained by repeating the coating preparation process for 6 cycles.

Unidirectional SiCf/SiC minicomposites with and without CaWO4 interphase coating were prepared through the polymer infiltration and pyrolysis (PIP) method. The schematic structure of the minicomposite is demonstrated in Fig. 1.

Schematic structure of the unidirectional SiCf/SiC minicomposite.

The flow chart for the preparation of SiCf/SiC minicomposites is shown in Fig. 2. The PIP process utilized polycarbosilane (PCS) to form SiC matrix on pyrolysis at 1100 °C in Ar24. The ceramic yield of PCS is about 81–85%, and its crystallization temperature is about 1000 °C. The choice of pyrolysis temperature was based on the balance of maximum matrix densification and minimum fiber degradation. For the impregnation and crosslinking process, firstly, SiC fibers were immersed into the slender crucible which contains PCS. Then, the crucible was transferred to the vacuum drying oven to complete the vacuum impregnation process, where continuous pumping can ensure more sufficient impregnation. After pumping for 2 h, the vacuum drying oven was slowly heated up to 130 °C to complete the vacuum crosslinking curing process. Apart from that, the SiC nanoparticles (40 nm) with a volume fraction of 30–40% were filled in PCS to reduce shrinkage cracking of the matrix during pyrolysis. The infiltration and pyrolysis process was repeated 7 times to improve the density of the minicomposites.

Preparation flow chart of SiCf/SiC minicomposites.

The composition of CaWO4 coated SiC fiber tows were examined by X-ray diffractometry (XRD, Ultimo IV, Riau, Japan). Morphology of coated SiC fibers and SiCf/SiC minicomposites was investigated by scanning electron microscopy (SEM, Inspect F50, FEI) equipped with energy dispersive spectroscopy (EDS). The porosity and density of SiCf/SiC minicomposites were measured through Archimedes' method of drainage.

In-situ SEM observation during the tensile tests of SiCf/SiC composites was performed using an SEM (Lyra3 GMU, Tescan, Czech Republic) in combination with an in-situ tensile stage (MTEST5000W, GATAN, UK) to investigate the fracture behavior of the composites. The composite specimens used for in-situ tests were approximately 1 × 2 × 15 mm in size, with their ends embedded in epoxy resin, and the area used for in-situ observation was approximately 2 × 4 mm. The samples were first gold sprayed (10 mA, 15 s, gold film thickness of approximately 2 nm) to increase the electrical conductivity before being placed in the SEM, and then the specimens were fixed on the tensile stage fixture (Fig. 3). In the in-situ tensile test, the stage used a displacement control mode, i.e., the motor loading rate was 0.1 mm/min until fracture. SEM imaging wad carried out using a backscattered electron detector with a working distance of 30 mm, a voltage of 10 kV, and beam current of 1 nA. An automatic image acquisition module with a single image acquisition time of about 3.2 s and an interval of 0 s was employed. The magnification chosen for in-situ observation was small, which can ensure that the sample was always within the field of view during the tensile process. After the sample fractured, the SEM still acquired several photographs to ensure that the whole process of stretching can be observed.

In-situ tensile SEM observation of SiCf/SiC minicomposite: (a) sample and (b) tensile platform.

Single fiber push-out tests were carried out to quantitatively characterize the interfacial property of SiCf/SiC minicomposites. The minicomposites were first ground and polished to 100–300 μm, and then the slice was fixed to the graphite flake with a groove. The thickness of the composite has been reported to not affect the estimation of the interfacial debonding stress25. Finally, Agilent Technologies G200 nano indention was utilized to push the single fiber in the composites. The maximum load is 1000 mN.

To evaluate the potential performance of the CaWO4 interphase in high-temperature oxidizing environment, the SiCf/CaWO4/SiC minicomposites were oxidized at 1000–1100 °C in air for 10 h and 50 h in the muffle furnace (SXL-1400). Furthermore, the composites were heat-treated at higher temperatures of 1200–1300 °C for 10 h and 50 h in air to investigate the compatibility between the CaWO4 coating and SiC.

According to the XRD analysis of CaWO4 coated SiC fiber shown in Fig. 4, only CaWO4 was identified besides the β-SiC phase originating from the underlying SiC fiber, suggesting that the prepared interphase coating is pure CaWO4.

XRD pattern of CaWO4 coated SiC fiber.

Figure 5 shows the surface morphology of the coated SiC fiber. Together with XRD, it can be confirmed that CaWO4 interphase coating was successfully prepared on SiC fibers. If compared to interphase coating fabricated by CVD methods, e.g. BN coating in7, the CaWO4 interphase coating prepared by the so-gel method is relatively rougher.

Surface morphology of CaWO4 coated SiC fiber.

The size of the unidirectional SiCf/SiC minicomposite prepared by the PIP method is about 2 × 3 × 20 mm. The cross-section view of SiCf/SiC minicomposites (SEM backscattered electron images) with and without the CaWO4 interphase coating is demonstrated in Fig. 6. As shown in Figs. 5, 6, there exist regions around the fiber with no interphase coating. Mud cracks often observed in composites prepared by the PIP method26 were also found in the current SiCf/SiC minicomposites as shown in Fig. 6. According to Fig. 6c,d, in the coated area the CaWO4 interphase coatings have a thickness in the range of 200–600 nm.

Cross-section view of SiCf/SiC minicomposites: (a,b) without interphase coating and (c,d) with CaWO4 interphase coating.

The density of SiCf/SiC minicomposites with and without the CaWO4 interphase coating is about 2.16 g/cm3 and 2.29 g/cm3, respectively, and their porosity is about 14.4% and 10% respectively. The higher porosity of SiCf/SiC composites with the CaWO4 interfacial coating is probably due to its influence on the impregnation efficiency of PCS. The distribution of CaWO4 interphase coating prepared through sol–gel method is relatively random and liable to aggregate on the fiber surface, which may obstruct the impregnation of PCS. The lower impregnation efficiency of PCS can cause less SiC matrix filled inside the fiber tow, which leads to the higher porosity of the SiCf/SiC minicomposite.

As one of the main functions of the interphase coating is to render pseudoplasticity to the composites, it is necessary to study the fracture behavior of the interphase-modified composite. As the prepared minicomposite samples were too small for carrying out reliable macroscopic tensile tests, the effect of the CaWO4 interphase coating on fracture behavior of SiCf/SiC minicomposites was mainly investigated by comparing the SEM fractography of the composite with and without the interphase. Fracture surfaces of the minicomposites are demonstrated in Fig. 7. The fracture surfaces of the minicomposite were generated through the in-situ tensile test as described in the experimental section. Flat fracture surfaces were obtained for the minicomposite without interphase coatings, and indications of crack deflection at the fiber/matrix interface or fiber pullout were not found (Fig. 7a,b). The SEM examination of the minicomposite without the interphase coating suggests clearly a brittle failure.

High-magnification fracture surface of SiCf/SiC minicomposites: (a,b) without interphase coating and (c,d) with CaWO4 interphase coating.

In the case of minicomposites reinforced with CaWO4 coated fibers, a rugged fracture surface was found. Debonding was observed to occur at the fiber/matrix interface, and distinct fiber pullouts were found on the fracture surface (Fig. 7c). In addition, SEM observation showed trough formation in the matrix after fiber pullout (Fig. 7d).

By comparing the fracture surface of SiCf/SiC minicomposites with and without CaWO4 interphase coating, it is indicated that CaWO4 interphase coating has a positive effect in changing the fracture behavior from a brittle manner to a more ductile one. When no interphase coating is present at the fiber/matrix interface, a strong bonding is formed, and as a result, cracks penetrate the fibers without any deflection during the failure of composites27,28,29. Hence, a flat fracture surface was obtained suggesting minimal fracture energy. In the SiCf/CaWO4/SiC minicomposite, the existence of CaWO4 interphase coating can provide a weaker interface bonding promoting the fiber/matrix interface debonding and fiber pullout during failure. Consequently, a rugged fracture surface was formed associated with the consumption of higher fracture energies.

The effect of the CaWO4 coating on the interfacial property of the minicomposites is further evaluated quantitatively through the fiber push-out test. Fibers located above the groove and surrounded by the matrix were chosen randomly for push-out tests. To facilitate the push-out experiment accounting for the potentially stronger fiber/matrix bonding, the SiCf/SiC minicomposites without interphase coating were ground and polished to a thinner slice allowing the use of lower push-out loads. Figure 8 shows the typical indentation curve of SiCf/SiC minicomposites with (Fig. 8a) and without interphase coating (Fig. 8b) obtained from the single fiber push-out test. A similar single fiber push-out curve was reported by Zhang et al. 25. According to the load–displacement curve, the push-out process of a single fiber in the SiCf/CaWO4/SiC minicomposite can be divided into four periods (A, B, C, and D) which were marked in the indentation curve (Fig. 8). Figure 9 indicates a schematic diagram of these four periods in the fiber push-out process25.

Representative indentation curve of single-fiber push-out tests on the SiCf/SiC minicomposite: (a) with CaWO4 interphase coating and (b) without interphase coating.

Adapted from reference25.

Schematic diagram of the fiber push-out process loaded by nanoindentation performed on the SiCf/CaWO4/SiC minicomposite.

In period A, the indenter presses into the SiC fiber, and the elastic deformation of SiC fiber occurs. The fiber/matrix interface is still in good condition with no cracks formed at the interface. During this period, the impact energy of the indenter is entirely assimilated by the elastic deformation of the SiC fiber25. In period B, partial debonding occurs at the fiber/matrix interface, and small cracks are formed at the interface caused by the decoupling of fiber and matrix. As a result, Young's modulus of the fiber/matrix system decreases as shown in Fig. 8. In period C, the fiber/matrix interface is entirely debonded. The fiber push-out is initiated and then SiC fiber is pushed below the surface of the slice. The critical load when SiC fiber is pushed out is denoted as, Pmax (Fig. 8). Finally, in period D, the indenter touches the surrounding SiC matrix causing the increase of Young's modulus of the system.

The interfacial debonding stress of SiCf/CaWO4/SiC minicomposite can be calculated as follows30, 31

where τ is the interfacial debonding stress, Pmax the push-out load, D the diameter of SiC fiber, and L the thickness of the slice.

About 15 push-out tests were carried out for the minicomposite. The average interfacial debonding stress of SiCf/SiC minicomposite with CaWO4 interphase coating and without interphase coating is calculated to be 80.7 ± 4.6 and 130.7 ± 0.1 MPa respectively, using Eq. (1). The interfacial debonding stress of composites with BN and PyC coating is about 5–20 MPa32, 33, and the debonding stress of composites with LaPO4 interphase is about 100–200 MPa34, 35. Lower interfacial debonding stress represents a weaker interface bonding and facilitates the toughening of the composites. Hence, the effectiveness of CaWO4 interphase for toughening is likely to be worse than BN or PyC coating but slightly better or close to the LaPO4 coating.

Based on the fracture surface investigation and interfacial debonding stress measurements, it is evident that the CaWO4 interphase indeed improved the interfacial property by providing a weaker bonding at the orginal fiber/matrix interface. It is noted, however, that the toughnening effect is not dramastic in the current work as indicated by the limited debonding length and matrix cracking observed from the fracture surface. This should be at least partly due to the localized incompleteness of the coating as seen in Fig. 6. It is believed that future optimization of the coating process would enable a complete utilization of the toughening effect provided by the CaWO4 interphase.

The SiCf/CaWO4/SiC minicomposite was oxidized at 1000 °C for 50 h and 1100 °C for 10 h and 50 h, and the cross-section view of the oxidized minicomposites is demonstrated in Fig. 10. According to the SEM observation, the CaWO4 interphase coating was still visible in the composite after the oxidation process, confirming that the CaWO4 interphase coating has a good oxidation resistance as expected. Hence, it can be speculated that CaWO4 interphase coating would be able to promote crack deflection and fiber pullout in the oxygen-rich environment for a long time.

Cross-section view of SiCf/CaWO4/SiC minicomposites oxidized at (a) 1000 °C for 50 h, (b) 1100 °C for 10 h, and (c) 1100 °C for 50 h.

In-situ tensile SEM observation of the SiCf/CaWO4/SiC minicomposite after being oxidized at 1100 °C for 50 h was carried out to evaluate the effectiveness of CaWO4 interphase coating after oxidation. Unoxidized SiCf/SiC minicomposite without the interphase coating was also investigated for comparison. SEM micrographs obtained in-situ during the tensile testing of the SiCf/SiC and oxidized SiCf/CaWO4/SiC minicomposite are shown in Figs. 11, 12, respectively. The entire failure process of SiCf/SiC minicomposite was completed within less than 2 s. It is obvious that the crack propagation path of SiCf/SiC minicomposite is almost perpendicular to the upper and lower surfaces of the composite, and the crack penetrates the fibers without any deflection (Fig. 11). The flat fracture surface of SiCf/SiC minicomposite is in accordance with the fracture surface morphology shown in Fig. 6.

In-situ tensile SEM observation of SiCf/SiC minicomposite without interphase coatings.

In-situ tensile SEM observation of SiCf/CaWO4/SiC minicomposite oxidized at 1100℃ for 50 h.

In comparison, crack deflection and apparent fiber pullout were indicated during the failure of SiCf/CaWO4/SiC minicomposite that has been oxidized at 1100 °C for 50 h (Fig. 12). Figure 13 further shows the fractography of SiCf/CaWO4/SiC minicomposite oxidized at 1100 °C for 50 h. Fiber pullout and fiber/matrix interface debonding were observed on the fracture surface which confirms that the CaWO4 interphase coating remains effective in toughening the minicomposite after oxidation. This is in high contrast to the PyC and BN coating, which are prone to be consumed by oxidation at intermediate temperatures leading to strong bonding at the fiber/matrix interface and the loss of crack deflection functionality36, 37.

Fractography of SiCf/CaWO4/SiC minicomposite oxidized at 1100 °C for 50 h.

The SiCf/CaWO4/SiC minicomposite was heat-treated at a higher temperature of 1300 °C for 50 h to evaluate the thermal compatibility between CaWO4 and SiC. The cross-section image and corresponding EDS map from the interface area are shown in Fig. 14. The CaWO4 interphase coating remains visible at the fiber/matrix interface and no obvious reaction zone is found between interphase and fiber or matrix. Meanwhile, the EDS mapping indicates the absence of Si in the interphase and W or O in the SiC matrix or fiber, which further confirms that no interfacial reaction happens after the heat treatment at 1300 °C for 50 h. Compared with the LaPO4 coating that has been shown reacting with SiC at 1200 °C15, the good thermal compatibility between CaWO4 interphase and SiC at 1300 °C suggests that CaWO4 interphase is more suitable for SiCf/SiC composites.

(a) Cross-section view of SiCf/CaWO4/SiC minicomposite heat-treated at 1300 °C for 50 h. (b–d) Corresponding EDS map scanning results.

Relatively uniform CaWO4 interphase coatings were prepared on the SiC fiber using the sol–gel dip-coating method and unidirectional SiCf/CaWO4/SiC minicomposites were then fabricated through the PIP method. The thickness of the interphase coating was in the range of 200–600 nm. The interfacial property of SiCf/CaWO4/SiC minicomposite was quantitatively evaluated and the thermal stability of CaWO4 interphase coating at 1000–1300 °C in air was investigated. The results are summarized as:

Crack deflection and fiber pullout are observed during the failure of the SiCf/CaWO4/SiC minicomposite, indicating that a weak fiber/matrix interface is provided by CaWO4 interphase coating. The interfacial debonding stress of SiCf/SiC minicomposite with the CaWO4 interphase coating is about 80.7 ± 4.6 MPa which is between that of PyC and LaPO4 coating.

Different from PyC and BN coating, the CaWO4 interphase coating is confirmed to have a good oxidation resistance. The CaWO4 interphase coating is preserved at the interface and can promote crack deflection and fiber pullout after the composite is oxidation at 1000–1100 °C for 10–50 h.

The CaWO4 interphase coating has no obvious interfacial reaction and diffusion with SiC fiber or matrix after heat treatment at 1300 °C for 50 h, suggesting its better thermal compatibility with SiC than the LaPO4 coating. Combined with the suitable interphase bonding stress, the CaWO4 interphase coating has a good potential to be used in SiCf/SiC composites.

Datasets used or analyzed during the current study are available from the corresponding author on a reasonable request.

Snead, L. L., Jones, R. H., Kohyama, A. & Fenici, P. Status of silicon carbide composites for fusion. J. Nucl. Mater. 233–237(part-P1), 26–36 (1996).

Article ADS Google Scholar

Hinoki, T., Zhang, W., Kohyama, A., Sato, S. & Noda, T. Effect of fiber coating on interfacial shear strength of SiC/SiC by nano-indentation technique. J. Nucl. Mater. 258, 1567–1571 (1998).

Article ADS Google Scholar

Yoshida, K., Matsukawa, K., Imai, M. & Yano, T. Formation of carbon coating on SiC fiber for two-dimensional SiC f/SiC composites by electrophoretic deposition. Mater. Sci. Eng. B 161(1), 188–192 (2009).

Article CAS Google Scholar

Kerans, R. J., Hay, R. S., Parthasarathy, T. A. & Cinibulk, M. K. Interface design for oxidation-resistant ceramic composites. J. Am. Ceram. Soc. 85(11), 2599–2632 (2002).

Article CAS Google Scholar

Chen, S. A., Zhang, Y., Zhang, C., Dan, Z. & Zhang, Z. Effects of SiC interphase by chemical vapor deposition on the properties of C/ZrC composite prepared via precursor infiltration and pyrolysis route. Mater. Des. 46(4), 497–502 (2013).

Article CAS Google Scholar

Chen, S. et al. Effects of polymer derived SiC interphase on the properties of C/ZrC composites. Mater. Des. 58, 102–107 (2014).

Article CAS Google Scholar

Sun, E. Y., Lin, H. T. & Brennan, J. J. Intermediate-temperature effects on boron nitride-coated silicon carbide-fiber-reinforced glass-ceramic composites. J. Am. Ceram. Soc. 80(3), 609–614 (2010).

Article Google Scholar

Naslain, R. et al. Boron nitride interphase in ceramic-matrix composites. J. Am. Ceram. Soc. 74(10), 2482–2488 (1991).

Article CAS Google Scholar

Tressler, R. E., Messing, G. L., Pantano, C. G. & Newnham, R. E. Tailoring Multiphase and Composite Ceramics (Springer, 2012).

Google Scholar

Cofer, C. G. & Economy, J. Oxidative and hydrolytic stability of boron nitride — A new approach to improving the oxidation resistance of carbonaceous structures. Carbon 33(94), 389–395 (1995).

Article CAS Google Scholar

Davis, J. B., Hay, R. S., Marshall, D. B., Morgan, P. & Sayir, A. Influence of interfacial roughness on fiber sliding in oxide composites with la-monazite interphases. J. Am. Ceram. Soc. 86, 305–316 (2003).

Article CAS Google Scholar

Fair, G. E., Hay, R. S. & Boakye, E. E. Precipitation coating of monazite on woven ceramic fibers: I. Feasibility. J. Am. Ceram. Soc. 90(2), 448–455 (2007).

Article CAS Google Scholar

Fair, G. E. et al. Precipitation coating of monazite on woven ceramic fibers: III—Coating without strength degradation using a phytic acid precursor. J. Am. Ceram. Soc. 93(2), 420–428 (2010).

Article CAS Google Scholar

Boakye, E. E. et al. Monazite coatings on SiC fibers I: Fiber strength and thermal stability. J. Am. Ceram. Soc. 89(11), 3475–3480 (2006).

Article CAS Google Scholar

Cinibulk, M. K., Fair, G. E. & Kerans, R. J. High-temperature stability of lanthanum orthophosphate (Monazite) on silicon carbide at low oxygen partial pressures. J. Am. Ceram. Soc. 91, 2290–2297 (2010).

Article Google Scholar

Shanmugham, S., Stinton, D. P., Rebillat, F., Bleier, A., Besmann, T. M., Lara‐Curzio, E., Liaw, P. K. Oxidation‐resistant interfacial coatings for continuous fiber ceramic composites. In Proceedings of the 19th Annual Conference on Composites, Advanced Ceramics, Materials, and Structures-A: Ceramic Engineering and Science Proceedings, Vol. 16.

Lee, W. Y., Lara-Curzio, E. & More, K. L. Multilayered oxide interphase concept for ceramic-matrix composites. J. Am. Ceram. Soc. 81(3), 717–720 (1998).

Article CAS Google Scholar

Mogilevsky, P., Parthasarathy, T. A. & Petry, M. D. Anisotropy in room temperature microhardness and fracture of CaWo4 scheelite. Acta Mater. 52(19), 5529–5537 (2004).

Article ADS CAS Google Scholar

Wu, B., Ni, N., Fan, X., Zhao, X. & Xiao, P. Scheelite coatings on SiC fiber: Effect of coating temperature and atmosphere. Ceram. Int. 47(2), 1693–1703 (2021).

Article CAS Google Scholar

Wu, B. et al. Strength retention in scheelite coated SiC fibers: Effect of the gas composition and pre-heat treatment. J. Eur. Ceram. Soc. 40(8), 2801–2810 (2020).

Article CAS Google Scholar

Hay, R. S. Monazite and scheelite deformation mechanisms. In 24th Annual Conference on Composites, Advanced Ceramics, Materials, and Structures: B: Ceramic Engineering and Science Proceedings, 203–217 (2000).

Goettler, R. W., Sambasivan, S., Dravid, V. P. Isotropic complex oxides as fiber coatings for oxide-oxide CFCC. In Proceedings of the 21st Annual Conference on Composites, Advanced Ceramics, Materials, and Structures—A: Ceramic Engineering and Science Proceedings, 279–284 (1997).

Chai, Y., Zhou, X. & Zhang, H. Effect of oxidation treatment on KD–II SiC fiber–reinforced SiC composites. Ceram. Int. 43(13), 9934–9940 (2017).

Article CAS Google Scholar

Huang, Z., Dong, S., Yuan, M. & Jiang, D. Manufacturing 2D carbon-fiber-reinforced SiC matrix composites by slurry infiltration and PIP process. Ceram. Int. 34, 1201–1205 (2008).

Article Google Scholar

Zhang, L., Ren, C., Zhou, C., Xu, H. & Jin, X. Single fiber push-out characterization of interfacial mechanical properties in unidirectional CVI-C/SiC composites by the nano-indentation technique. Appl. Surf. Sci. 357(DEC.1PT.B), 1427–1433 (2015).

Article ADS CAS Google Scholar

Zok, F. W. Ceramic-matrix composites enable revolutionary gains in turbine engine efficiency. Am. Ceram. Soc. Bull. 95(5), 22–28 (2016).

CAS Google Scholar

Boakye, E. E. et al. Evaluation of SiC/SiC minicomposites with yttrium disilicate fiber coating. J. Am. Ceram. Soc. 101(1), 91–102 (2018).

Article CAS Google Scholar

Chawla, K. K. Ceramic Matrix Composites 212–251 (Springer, 1998).

Google Scholar

Krenkel, W. Ceramic Matrix Composites: Fiber Reinforced Ceramics and Their Applications (Wiley, 2008).

Book Google Scholar

Yang, W., Kohyama, A., Noda, T., Katoh, Y. & Yu, J. Interfacial characterization of CVI-SiC/SiC composites. J. Nucl. Mater. 307(2), 1088–1092 (2002).

Article ADS Google Scholar

Tandon, G. P. & Pagano, N. J. Micromechanical analysis of the fiber push-out and re-push test. Compos. Sci. Technol. 58(11), 1709–1725 (1998).

Article CAS Google Scholar

Cao, H. et al. Effect of interfaces on the properties of fiber-reinforced ceramics. J. Am. Ceram. Soc. 73(6), 1691–1699 (1990).

Article CAS Google Scholar

Curtin, W. A., Eldridge, J. I. & Srinivasan, G. V. Push-out tests on a new silicon carbide/reaction-bonded silicon carbide ceramic matrix composite. J. Am. Ceram. Soc. 76(9), 2300–2304 (1993).

Article CAS Google Scholar

Morgan, P. E. & Marshall, D. B. Ceramic composites of monazite and alumina. J. Am. Ceram. Soc. 78(6), 1553–1563 (1995).

Article CAS Google Scholar

Kuo, D.-H., Kriven, W. M. & Mackin, T. J. Control of interfacial properties through fiber coatings: Monazite coatings in oxide-oxide composites. J. Am. Ceram. Soc. 80(12), 2987–2996 (1997).

Article CAS Google Scholar

Wang, L. Y., Luo, R. Y., Cui, G. Y. & Chen, Z. F. Oxidation resistance of SiCf/SiC composites with a PyC/SiC multilayer interface at 500 °C to 1100 °C. Corros. Sci. 167, 108522 (2020).

Article CAS Google Scholar

Bertrand, S., Pailler, R. & Lamon, J. Influence of strong fiber/coating interfaces on the mechanical behavior and lifetime of Hi-Nicalon/(PyC/SiC)n/SiC minicomposites. J. Am. Ceram. Soc. 84, 787–794 (2001).

Article CAS Google Scholar

Download references

This work was supported by the National Natural Science Foundation of China (No. 52072238).

School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai, 200240, China

Na Ni

School of Material Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, China

Na Ni, Binbin Wu, Yinchun Shi, Xiaohui Fan & Chuanwei Li

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

N.N and B.B.W designed and performed the experiments, and analyzed the data. N.N and C.W.L supervised this study. All the authors discussed the results., and wrote and reviewed the manuscript text.

Correspondence to Na Ni or Chuanwei Li.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Ni, N., Wu, B., Shi, Y. et al. Interfacial properties of SiCf/SiC minicomposites with a scheelite coating. Sci Rep 12, 21950 (2022). https://doi.org/10.1038/s41598-022-26626-9

Download citation

Received: 13 August 2022

Accepted: 16 December 2022

Published: 19 December 2022

DOI: https://doi.org/10.1038/s41598-022-26626-9

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.