Plasma electrolytic oxidation (PEO) is a surface-treatment process extensively used to protect the surfaces of light metals such as Mg, Al, and Ti. Here, we report an environmentally friendly PEO process that uses nitrogen-containing electrolytes and low voltages (120 V) to form ~ 12 micron thick, uniform, adherent and porous oxide coatings on T1 titanium alloy surfaces. We evaluated the influence of nitrogenation by comparing the coatings to alloys treated in PEO baths without nitrogen-containing compounds. Both sets of samples exhibited basalt-like morphologies with distinct variation in the pore structures. The composition analyses showed that the coatings were primarily composites of titanium oxides and silicates. The T1 Ti alloys treated with nitrogen-containing electrolytes also contained TiC and TiN. This is the first ever report of producing TixOy, Ti–Si–O, TiC, and TiN composite coatings using a single PEO bath without carbide/nitride nanoparticles. The bandgaps of the coatings suggested visible light functionality. The use of nitrogen-based compounds in the PEO baths improved the hardness of the oxide layers but introduced stress-induced cracking which are potentially responsible for the reduction in corrosion resistance of the nitride and carbide containing coatings.

Plasma electrolytic oxidation (PEO) is a surface-treatment process used to protect metallic substrates by inducing the formation of environmentally inert oxide coatings. The process applies a high direct current (DC), pulsed DC or alternating current (AC) voltage between a stable cathode and the target substrate in an electrolytic bath. Micro-arc discharge channels on the substrate surface form the oxide coating. The primary objective of PEO surface treatments is to provide metallic substrates with wear and corrosion resistance. A unique feature of the PEO process is that plasma thermochemical interactions at multiple-surface discharges result in the bimodal growth of oxide coatings. The PEO treatment processes simultaneously form a porous layer on the substrate which extends a few microns into the bulk of the substrate forming a highly adherent corrosion resistant coating. Magnesium, aluminium, and titanium alloys are among light metals commonly subjected to PEO surface treatments1. Recent reviews also report the use of PEO surface treatments for copper, zinc and niobium alloys2.

Titanium and its alloys have a diverse range of applications in aerospace, chemical, biomedical3,4 and semiconductor industries because of their high specific strength, low density, ease of fabrication and biocompatibility. T1 titanium alloys are of particular interest for scientific5 and industrial applications as they possess lower elasticity and superior corrosion resistance compared to other titanium alloys. T1 alloys are not directly treatable with standard surface engineering processes as they neither respond to thermal hardening processes nor are they reactive with oxygen. Thermochemical surface treatment processes available for enhancing the wear and corrosion resistance of Ti alloys include physical vapor deposition (PVD), chemical vapor deposition (CVD), chemical conversion, anodization, electroplating, electroless plating, polymerization of organic coatings and PEO. Surface treating titanium alloys by PEO is a well-known, commercially viable process as PEO can develop thick, adherent, wear resistant oxidized coatings on the alloy surface. Other surface-treatment processes for titanium alloys are carburizing and nitriding. Carbonization of titanium alloys produces a micron-scale TiC coating and requires high processing temperatures (> 1000 °C)6. Nitriding titanium alloys results in the formation of extremely hard Ti–N coatings (1500 to 3000 HV), and the process requires controlled N2-rich environments7. The downside to direct nitridation of titanium alloy surfaces is the reduction of their fatigue strength8.

PEO coatings on titanium are of high interest due to their ductility, corrosion resistance, and especially photocatalytic nature. Scientific interest in titanium oxides and titanium oxide-based materials was piqued by the discovery of the ability of TiO2 to split water under UV-light9. This discovery prompted a vast amount of research on TiXOY-based photocatalysts for self-cleaning applications, energy harvesting applications and organic pollutant decomposition10. Most TiO2-based materials reported in the literature are nanoparticles and require additional processing for real world applications. Efficient functionalization of titanium oxides also requires the materials to be both responsive under visible light and mechanically robust.

Functionalization techniques for Ti–O-based materials include process-induced nanostructured arrays, surface crystallization, and micro/nanoparticle incorporation into PEO-treated ceramic coatings. Uhm et al., reported producing PEO-tailored titania nanotubes sputtered with Ag for antimicrobial applications. The authors reported that the functionalized coatings reduced S. aureus cell viability11. Jiang et al., produced nickel titanate nanowires with controllable sizes for catalytic CO oxidation12. Ti alloys undergo surface crystallization when treated with plasma techniques for surface protection. Benčina et al., report that controlling plasma conditions can induce phase-initiation or transition between anatase and rutile TiO23. Studies show multi-phase TiO2 coatings exhibit enhanced photocatalytic and energy harvesting applications when compared to pure phase anatase or rutile-based coatings13. Addition of micro/nanoparticles to PEO baths is one of the more recent techniques for functionalizing surface treated T1 Ti alloys. Incorporating nanoparticles such as Ag, Cu and Zn14 into PEO-treated Ti alloys by electrolyte modification improved the antibacterial performance, corrosion resistance behaviour and bio-integration applicability of the materials. Non-metallic particles such as SiO2, Si3N4, SiC, Al2O3 and ZrO2 and graphene nanoparticles reportedly improved the mechanical functionality of Ti-alloyed components for aerospace applications. Literature studies also report incorporating NiO, Fe2O3, Cr2O3, and hydroxyapatite15 microparticles into the electrolytic baths to produce functional ceramic oxide coatings on titanium and/or titanium alloys.

Silicate compounds are commonly used constituents for PEO electrolytes, and few studies report the combined influence of these compounds on functionalizing ceramic oxide coatings formed by surface treating T1 alloys16. PEO-coated titanium implants, prepared using a silicate containing electrolyte, exhibited higher osseointegration in rat models than raw-titanium implants17. Shokoufar et al., reported enhanced mechanical behaviour of PEO-treated Ti–6Al–4V surfaces. The authors incorporated carbide content into the ceramic coating by adding SiC nanoparticles to the PEO electrolyte. The study also showed that incorporation of nanoparticles into the PEO-treated coatings negatively impacted the friction coefficient and corrosion current density of the oxidized materials18. Chen et al., reported a two-step process of producing carbon incorporated PEO treated titanium oxide coatings with improved tribological behaviour. The authors used magnetron sputtering to deposit diamond-like carbon into the micropores of PEO-treated commercial grade-2 titanium metal19. Nitrogenation of TiO2-based ceramic coatings is another well-researched method for improving their functionality; however, there are no reports of incorporating nitride content into PEO-treated titanium alloys by modifying the electrolyte composition.

Cirrus aimed to design a single low power PEO process for light metal surface modification. Our mission was to improve the versatility and simplicity of PEO processes while staying ahead of the environmental and sustainability benchmarks. The current study addresses the need for surface treatment process that directly protect T1 titanium alloys with a thin ceramic oxide coating using low energy and benign electrolytic chemicals. The PEO surface treatment methodology described here produces functional ceramic coatings on T1 Ti alloys using voltages less than 120 V and environmentally friendly silicate-containing organo-alkaline baths. Our PEO technology produces nitrogenated coatings in electrolytes containing trace amounts of aminophenol20. The high-growth rate coatings (~ 40 μm/h) are composites of titanium oxides, carbides, nitrides, and silicate compounds. We were particularly interested in analysing the influences of carbide and nitride compounds on the functionality of the ceramic coatings. To the best of our knowledge, there have been no previous studies on combining silicates and nitrogen-based compounds in a single PEO electrolyte to produce functional titanium oxide-based composite coatings on T1 Ti alloys.

Figure 1a shows the variation of voltage during the PEO treatment of the T1 titanium alloys. The unique feature of this process is that the surface treatment requires less than 120 V. We treated two sets of T1 titanium alloys using the PEO technology reported in this paper. Figure 1b is an image of as-received T1 titanium alloy machined to the required dimensions. Samples labelled Ti-A (Fig. 1c) were prepared using silicate-containing organo-alkaline baths. PEO treatment caused the samples to develop a uniform bluish-grey ceramic coating on the surface. Samples prepared using silicate and aminophenol in the organo-alkaline bath chemistry are labelled Ti-B (Fig. 1d).

(a) Voltage vs time graph demonstrating the low energies required to produce oxide coatings on T1 Ti alloys using eco-friendly PEO electrolytic baths. (b) As-received T1 Ti alloy machined to 8 mm × 20 mm × 0.1 mm substrate dimensions for PEO treatment. (c) PEO-treated T1 alloys with silicates in the organo-alkaline bath. The ceramic coating, Ti-A, is continuous and bluish grey in appearance. (d) PEO treated T1 alloys with silicates and aminophenol in the organo-alkaline bath (Ti-B). The coatings, Ti-A and Ti-B, appear to be visually similar. Photo credit: F. Hou (b–d).

Macroscopically, Ti-A and Ti-B possess similar appearing bluish-grey ceramic coatings. Scanning electron microscopy (SEM) images of the Ti-A and Ti-B surfaces showed that the addition of aminophenol to the PEO bath induced microscale morphological changes to the surfaces. Ti-A surface (Fig. 2a) exhibited cracks and pores typical of a ceramic oxide coating16,21. The pore sizes ranged from < 1.00 to 3.00 μm. The image also shows that the Ti-A pore distribution is non-uniform as illustrated by cross-sectional image provided in Fig. 2c. The surface for Ti-B (Fig. 2b) has cracks and pores integral to oxidized layers but the pore-structure here appears denser. The formation of oxide films during PEO treatments is a facile yet complex process. The application of voltage between the Ti substrate and the electrolyte initially leads to formation of an insulating barrier layer on the surface. Once the applied voltage exceeds the breakdown potential of the barrier layer, conductive discharge channels form. Elevated temperatures in the discharge channels lead to the melting and oxidation of subsurface alloy elements. Molten oxides transported through the discharge channels instantaneously solidify producing the basalt-like morphology observed on Ti-A and Ti-B coatings. The coatings thicken as the process continues. Growth kinetics of PEO-treated surfaces suggest that porosity of the coatings increases linearly with thickness22. In this study, we observe that the addition of aminophenol to PEO electrolyte refines the porosity without influencing the growth-rate of Ti-B coating. The electrolyte modification enabled a greater control in pore dimensions on Ti-B surface due to the surfactant-like behaviour of aminophenol. Our hypothesis is that reduction in the gas bubble dimensions is due to variations in arc-discharge intensity, temperatures and pressures in the discharge channels caused by aminophenolic modification of the PEO electrolyte. The changes in electrolyte properties also appear to increase the uniformity and density of discharge channels on the surface. The result—a high porosity coating with controlled morphology observed in Ti-B (Fig. 2b)23. The reduction in pore dimensions result in less molten oxide transport per discharge channel. The higher porosity on Ti-B coating, manifesting as more prominent surface cracks, may influence the corrosion properties. Figure 2d shows propagation of surface cracks on Ti-B through the thickness of the coating. The modified microstructure of Ti-B coatings, due to addition of nitrogen-containing compounds in the PEO bath, could potentially enhance the mechanical performance of the coatings.

(a) Surface morphology of Ti-A: the figure shows the porous oxide layer on T1 alloy treated in PEO bath. The cracks and variation in the pore sizes are typical of a treated Ti surface. (b) Surface morphology of Ti-B: addition of aminophenol to the PEO bath modified the pore structure of the PEO-treated Ti coating. The pores are relatively uniform in size and appear to have a more uniform distribution on the surface. (c) Cross-sectional morphology of Ti-A showing the pore-distribution along the depth of the coating. (d) Cross-sectional morphology of Ti-B; the pore distribution is more uniform compared to Ti-A. Additionally, the image also shows the propagation of surface cracks through along the depth of the coating.

We characterised the crystallographic and compositional properties of Ti-A and Ti-B using X-ray diffraction (XRD) and surface enhanced Raman spectroscopy (SERS). We compared the XRD patterns of Ti-A and Ti-B coatings with that of an untreated Ti alloy to isolate the signals from substrate. XRD patterns in Fig. 3a show that surfaces oxidised in PEO baths containing aminophenol exhibit similar crystallographic signatures to those treated in baths without aminophenol. Most of the peaks correspond to anatase and rutile phase TiO2. The peaks for TiO2 and Ti2O3 appear to coincide at ~ 53°.

(a) XRD patterns of Ti-A and Ti-B. The patterns show that the addition of aminophenol to the bath chemistry has no influence on the crystallographic signature of the formed oxide layer. (b) Raman spectrum of Ti-A with peak deconvolution. (c) Raman spectrum of Ti-B with peak deconvolution. The amorphous carbon signature detected in the oxidized layer is due to the addition of aminophenol to the PEO bath. (d) List of functional groups associated with the Raman bands observed in deconvoluted SERS spectra.

XRD patterns for Ti-A and Ti-B are similar, thus indicating that aminophenol modification of the electrolyte has little influence on the crystallographic properties of the coatings. A future study is focused on the possible enhancement of crystal plane orientation due to the influence of substrate crystallography, electrolyte composition and coating growth-rate. Coating growth-rates in PEO processes are high for silicate-containing electrolytes24. However, the current results do not provide us with sufficient data to analyse the crystallographic orientation.

Figure 3b,c illustrate the Raman spectra of Ti-A and Ti-B samples treated in PEO baths without and with aminophenol, respectively. Figure 3d provides a list of functional groups associated with the deconvoluted peaks. The spectral deconvolutions for Ti-A and Ti-B spectra show that the coatings are composites of aluminium, silicon, and titanium oxides, titanium silicate and organic compounds. Additionally, we detect amorphous carbon in the Ti-B coating. Ti-A and Ti-B exhibit a sharp peak for anatase phase TiO2 at ~ 140 cm−1. This compliments the observation of oriented anatase crystal planes from XRD patterns. The detection of TiSiO4 concurs with the XRD results for both Ti-A and Ti-B coatings25. The spectrum for Ti-B (Fig. 3c) shows that the oxide coating contained amorphous carbon and other organic compounds. The appearance of the amorphous carbon peaks in the spectrum suggested the potential carbonization of the oxide layer during the PEO process. The peaks at ~ 515 cm−1 and ~ 570 cm−1 suggest the presence of TiC26 and TiN27 in the Ti-B coatings. The absence of peaks corresponding to TiC in the XRD pattern for Ti-B is due to insufficient intensity from carbide particles for reliable detection. Another possibility is that the TiC particles are not oriented to the direction of the incident X-rays.

We used X-ray photoelectron spectroscopy (XPS) for advanced analysis of Ti-A and Ti-B samples. We collected core-loss spectra for C, N (Ti-B only), O, Si and Ti. Figure 4 provides Ti-A core-level spectra. Peak analysis for the samples referenced the C 1 s peak at 283 eV (Fig. 4a). The peak deconvolutions exhibited the presence of C–C bonds at ~ 283 eV and C–O–C bonds at ~ 284 eV both of which correspond to adventitious carbon content accumulated on the coating surface. We observed a low-intensity broad peak corresponding to carboxylate bonds at ~ 287 eV. Ti-A samples also contained minute amounts of sp2 bonded carbon in the oxidized coating. We hypothesize that the citrates in PEO bath have the potential to carbonize the ceramic coating to a small extent. Deconvoluted O 1s peaks (Fig. 4b) showed the presence of metal oxides at ~ 528 eV, metal carbonates at ~ 529 eV, and C–O bonds ~ 530 eV. The peak at 530 eV corresponds to adventitious content accumulated on the coating surface. The low intensity peak at ~ 534 eV corresponds to Na KLL. Si 2p spectrum (Fig. 4c) deconvolution resulted in two peaks. The peak at ~ 101 eV corresponds to SiO2 and the one at ~ 100 eV indicates the presence of organic silicon content in the coating. Ti 2p spectrum (Fig. 4d) exhibited a shape normally representative of TiO2 with a small amount of Ti2O3. Surface compositional analysis indicated that Ti-A samples are composite ceramic coatings prepared in a PEO bath capable of introducing mechanically strengthening Si–O-containing compounds. We added nitrogen-containing compounds to the bath chemistry with an aim to further enhance the mechanical and functional properties of the oxide coatings.

XPS core-loss spectra for Ti-A. (a) XPS spectrum showing the C 1s peak located at ~ 283 eV. The signature primarily corresponds to adventitious carbon. We observe a low intensity peak corresponding to polymeric C=O at ~ 287 eV. (b) Deconvoluted XPS peaks for oxides in the PEO-treated coating. The peaks at ~ 529 eV are signals from adventitious C=O and C–O and from any metal carbonates in the coating. (c) Deconvoluted Si 2p peaks showing signatures for organic Si (~ 100.4 eV) and SiO2. (d) We observe XPS peaks for TiO2 and Ti2O3 in the core-loss spectra collected for Ti 2p. Also observed in the figure is the satellite feature at ~ 471 eV typical of titanium oxides.

Figure 5 provides XPS core-level peaks for Ti-B samples. The shapes of peaks for C, O, Si and Ti are noticeably different between Ti-A and Ti-B. Figure 5b,e indicated the nitrogenation of the coating composition. We hypothesize that the incorporation of nitrides in Ti-B coatings is due to the influence of arc energy generated at the alloy surface in the nitrogen containing PEO bath. We analysed XPS core-level spectra for Ti-B with reference to the C 1s (C–C) peak at ~ 284 eV (Fig. 5a). Deconvolution of C 1s spectrum resulted in four distinct peaks; the first peak at ~ 282 eV suggests the presence of metal carbides and the one at ~ 287 eV indicates the presence of polymeric C=O bonds in the Ti-B coatings. The other two peaks, C–C at ~ 284 eV and C–O–C at ~ 285 eV, correspond to the presence of adventitious carbon content on the coating surface. XPS spectrum for N 1s in Ti-B coatings exhibited two deconvoluted peaks (Fig. 5b); the peak at ~ 396 eV suggests the presence of a small amount of metal nitride in the composition. The peak at ~ 399 eV indicates that most of the nitrogen signature is from silicon oxynitride content in Ti-B coatings. O 1s spectrum for Ti-B has a complex shape and the peak deconvolution resulted in four peaks (Fig. 5c). The peaks at ~ 527 eV and ~ 529 eV indicate the presence of metal-oxides in Ti-B coatings. The peak at ~ 531 eV corresponds to the C–O bonds in the coating typical of adventitious contamination. Finally, we observe the Na KLL peak at ~ 535 eV. The Si 2p core-level spectrum collected from Ti-B samples had a slightly asymmetrical shape (Fig. 5d). Peak deconvolution showed that the Si content in the coatings is primarily in the form of TiSiOX (~ 102 eV). The deconvolution also suggested the presence of of Si3N4 (~ 100 eV). Figure 5e shows the XPS spectrum for Ti 2p in the Ti-B coatings; the spectrum has a complex shape and the deconvolution resulted in four distinct peaks. The peaks at ~ 457 eV and ~ 463 eV correspond to the Ti 2p3/2 and Ti 2p1/2 in TiO2. The peak at ~ 461 eV corresponds to Ti2O3. The interesting feature in this spectrum is the peak at ~ 455 eV suggesting the presence of TiN27 and TiC28 in the coating. These results support the XRD, and SERS data presented for Ti-B in Fig. 3a,c.

XPS spectra for Ti-B. (a) The C 1s peak for the coatings oxidized with aminophenol in the PEO bath is at ~ 284 eV. The peak at ~ 282 eV indicates the presence of Ti-C in the coating. (b) Core-loss peak for N 1s shows the presence of metal nitrides in the coating, potentially synthesized under the influence of arc energy in generated by nitrogen-containing PEO bath. Additionally, we also observe a low intensity peak for NSi2O at ~ 399 eV. (c) XPS peaks for O1s correspond to the presence of metal oxides and adventitious material on the coating surface. (d) XPS spectra for Si2p indicate that the ceramic layer contains TiSiOX and potentially Si3N4. (e) Ti2p core-loss peaks exhibit a complex shape. The coating is primarily composed of titanium oxides. The minor satellite feature at ~ 459 eV is due to the presence of Ti–N bonds in the coating. The peak at ~ 455 eV corresponds to the presence of Ti–C bonds.

The material transfer through the discharge channels generated during PEO treatments is bi-directional. We state in earlier sections that the molten oxides transport occurs from the subsurface to the surface. The localized elevated temperatures decompose the electrolyte constituents leading to the incorporation of polycondensed silica ions into the discharge channels. We assume this phenomenon is also responsible for incorporation of organic compounds (citrates) into Ti-A and Ti-B coatings. Decomposition of aminophenol, in the discharge channels, explains the incorporation of nitride and carbide content into Ti-B. Most research studies rely on this mode of particle incorporation to enhance the functional, mechanical, and electrochemical properties of PEO-treated surfaces29.

We evaluated the mechanical properties of Ti-A and Ti-B coatings using nanoindentation. The results showed that the PEO process reported in this paper improved the hardness by approx. 1.5 times. Bare Ti-alloys possess hardness of 4.43 GPa. The coatings oxidized with and without aminophenol in the bath chemistry exhibited hardness values of 7.12 GPa and 6.63 GPa, respectively. This is a clear demonstration of the well-known enhancement in mechanical behaviour of T1 substrates via PEO-assisted surface modification30. The improved hardness of the treated alloys is due to the formation of a robust oxide layer reinforced by silicate particle incorporation. It is possible that the cracks observed on Ti-A and Ti-B are a result of silicate-induced brittleness24,31. TiC and TiN content in Ti-B coatings are responsible for their high hardness value32.

Figure 6 shows the diffuse reflectance spectra for Ti-A and Ti-B coatings prepared by surface treating T1 alloys in PEO baths with and without nitrogen-containing compounds. We used Kubelka–Munk theory to transform the reflectance spectra for generating Tauc plots. We assumed Ti-A and Ti-B coatings to possess direct bandgaps. The bandgap estimations of 2.79 eV for Ti-A and 2.76 eV for Ti-B are remarkably lower than commercially available TiO2 (3.0 to 3.2 eV). The results show that the coatings are potentially photocatalytic in the low-energy visible blue light (~ 446 nm) region. The smaller bandgap of Ti-A and Ti-B coatings is due to their silicate and organic content. Vasilyeva et al. report that silica/titania composites exhibit catalytic conversion properties with 97% efficiency; while nitrogen-doping33 and carbonization34 of titanium oxide-based coatings are popular routes of enhancing their functional properties for various semi-conductor applications. The current bandgap reduction is limited, yet the process shows promise for developing photocatalytic materials. We are currently studying the coatings’ photocatalytic efficiency.

Diffuse reflectance spectra of Ti-A and Ti-B coatings. Spectra show that the coatings exhibit bandgaps in the visible blue light region (~ 446 nm). There is no variation in the bandgap for samples oxidized in PEO baths with and without nitrogen-containing compounds.

We extracted the corrosion potentials of the Titanium substrate, and the Ti-A and Ti-B coatings from the Tafel plots (Fig. 7). Figure 7b provides the extracted potentiodynamic test results. The Tafel results show that the untreated Ti alloy displays a less noble corrosion resistance as compared to Ti-A and Ti-B. Ti-A coating yields a less noble corrosion behaviour than Ti-B. The Tafel plots indicate the presence of nitrides and carbides in Ti-B have a positive influence on corrosion behaviour. SEM images of Ti-A and Ti-B (Fig. 2) reveal that the coatings are porous with surface cracks. These can propagate through the thickness of Ti-B coating and may negatively impact its corrosion resistance. Dissimilar materials combined with porosity in both Ti-A and Ti-B coatings may have a detrimental influence due to galvanic corrosion. Further work is required to optimize the process parameters to reduce the porosity of the surface coating to further improve their corrosion resistance.

(a) Tafel plots for Ti-A and Ti-B coatings. The curve for a bare T1 titanium alloy was also measured as a baseline. (b) The corrosion potentials and current densities extracted from the curves show that Ti-B is less susceptible to corrosion than Ti-A and the untreated Ti alloy.

It is important to acknowledge that while the icorrosion values are reported as current densities, this is done under the assumption that the entire exposed surface area (1 cm2) in the electrochemical cell is active. The increased surface area due to the porosity was not measured, therefore, real-world corrosion current densities are likely lower than the values reported in Fig. 7b.

Figure 8 demonstrates the impedance behaviour of PEO-treated Ti alloys compared that of untreated Ti substrates. We modelled the electrochemical impedance spectroscopy (EIS) response of untreated and PEO-treated substrates using the equivalent electrical circuits (EEC) illustrated by Fig. 8d,e. Rcoating, Rdiffusion, and Relec represent the coating, diffusion layer and electrolyte resistances respectively. CPEcoating and CPEdiffusion represent the constant phases elements (CPE) for coating and diffusion layers. The modelling of EIS results as an EEC is common for coatings on metal substrates. The porosity is represented by the parallel CPEdiffusion and Rdiffusion elements (Fig. 8e). Comparing Ti-A and Ti-B, the magnitude of impedances from each of the fitting elements (Fig. 8f) is seen to be larger for Ti-B, suggesting that addition of aminophenols has a positive influence on the corrosion resistance of Ti-B coatings.

Electrochemical impedance spectroscopy of Ti-A and Ti-B coatings compared to the electrochemical behavior of an untreated Ti alloy. (a) Nyquist plots; (b,c) Bode plots; (d) EEC model for untreated Ti alloy; (e) EEC models for Ti-A and Ti-B; (f) list of fitting parameters of EIS EECs obtained for untreated Ti alloy, Ti-A and Ti-B.

Pores, stress-induced cracks, and highly porous diffusion layers are typical of a PEO-treated metal substrate. One of our aims for using an aminophenol as PEO electrolyte modifier is to limit the formation of coating defects through the treatment process. We observed that nitridation and carburization of PEO treated coatings densifies the coating structure and mitigates the propagation of stress induced cracks (Fig. 2b,c). This phenomenon is evident from the EEC modelling parameters. The resistance of the Ti-B coating is approximately 5 times higher than Ti-A, but the diffusion layer resistance of Ti-B is lower than Ti-A. Hoche et al. proposed a model that explains the observed behaviour of our PEO-treated coatings35. The NaCl solution first penetrates the process-induced defects. The larger pore dimensions and propagating surface cracks on Ti-A are responsible for the poorer corrosion resistance of Ti-A than Ti-B. We also observe that the addition of aminophenols to PEO electrolytes increases the distribution of arc discharge channels on the substrate surface leading to a poorer corrosion resistance observed in Ti-B diffusion layer.

The objective of this study was to demonstrate the application of eco-friendly PEO bath chemistries in surface treatment of T1 Ti alloys. The surface treatment process described here produced uniform and adherent coatings on the substrate surface with interesting characteristics. The process also offered a single-step technique to incorporate nitride and carbide content into the surface oxides. Our bandgap analysis tests showed that the surface oxides produced during the PEO treatment process may have visible light photocatalytic applications. The oxide layers formed during PEO provided some unique corrosion-resistant properties to the T1 titanium substrates.

The morphology and composition of surface oxides using PEO baths were attributed to the non-equilibrium behaviour of reactive species generated under the influence of localized micro-arc discharge points at the T1 titanium alloy surfaces. PEO processes generate intense localized thermal energy fluxes that have a bi-modal influence on T1 Ti substrates. The direct oxidation of the substrate forms the porous structure of the oxide coating. The temperatures (~ 3000 °C)36 achieved during the PEO treatment process were sufficient to melt the substrate surface and create the basalt-like appearance of the oxide layers. The uniform pore distribution in the surface oxide layer was important for the coating to protect the underlying substrate from corrosion. We found that surface treatment with nitrogen compound-containing PEO bath has improved the pore density of the resultant oxide layer while preserving the basalt-like morphology of the coating. However, the hardening of the Ti-B coatings produced using the aminophenol-enhanced PEO bath has also caused stress-induced cracks to appear on the surface.

The novelty of the Ti-B coatings lies in the fact that adding nitrogen-containing compounds to the bath chemistry rather than C4−- or N3−-based nanoparticles has improved the uniformity in pore distribution. Our hypothesis is that the presence of nitrogen-based chemicals in the bath chemistry caused a phenomenon similar to the nitrogenation treatment reported by Shen et al.37. The results from compositional analyses presented in this paper show that nitrogenation of the PEO-treated surfaces can be achieved using eco-friendly chemicals and at low oxidation voltages. Carburization of coatings was also achieved without the post-processing the PEO-treated surfaces19. To the best of our knowledge, there are no other reports on the preparation of TiC containing PEO coatings using organic electrolytic baths.

Referring to the SEM images of Ti-A (Fig. 2a) and Ti-B (Fig. 2b) it appears that Ti-B has cracks which reduced the corrosion protection of the PEO coating in comparison to Ti-A. The presence of carbides and (oxy-)nitrides in the coating, as shown in the XPS measurement data (Fig. 4), would indicate more brittle mechanical properties. The mechanical testing showed the Ti-B coating to be approximately 7.5% harder than Ti-A. The surface carbides and (oxy-)nitrides will introduce brittle character to the Ti-B coating which would explain the many cracks visible in the Ti-B coating.

Ti-A and Ti-B coatings exhibit bandgaps of < 2.8 eV suggesting that the materials have visible light (λ = ~ 440 nm) photoactivity. This remarkable reduction of TiO2 bandgap from ~ 3.1 eV is due to the presence of silicate and carbon-containing compounds in Ti-A and silicate, carbon, and nitrogen-containing compounds in TiB. Similar functionalization of PEO-treated titanium alloys, reported by few other research groups, was only obtained by incorporating nitride or carbon-containing compounds prior to or post PEO-treatment. Lin et al. produced N-doped TiO2 visible light photocatalysts using a TiN seed layer on Ti foils subjected to PEO surface treatment38. Tao et al. functionalized PEO-treated Ti alloys by thermal polycondensation of graphitic C3N4 onto the oxidized substrates39.

Cirrus PEO technology has an overall positive influence on the electrochemical behaviour of treated Ti substrates. Stress-induced cracks in Ti-A and Ti-B may be detrimental to the corrosion resistance of the coatings. The potentiodynamic behaviour of Ti-A coatings was in accordance with similar materials reported in the literature2. The much lower corrosion of Ti-B compared to Ti-A is attributed to the reduction in pore dimensions and densification of the coating due to nitridation and carburization.

The results presented in this paper suggest that light metals can be reliably protected using low energy PEO processes and eco-friendly electrolytes. We demonstrated a facile method to incorporate carbon and nitrogen-compounds into titanium oxide coatings to achieve visible light functionalization. The corrosion behaviour of the coatings was unexpected and requires further research. We are currently working on mitigating stress-induced cracking of the nitride and carbide-coatings during PEO processing. We are currently researching the applicability of the PEO technology (patent pending) reported in this paper for a wide range metal alloys such as Mg, Al, and mild steel.

We used T1 Ti alloys measuring 20 mm × 8 mm × 0.1 mm in dimensions the study reported here. Prior to treatment by PEO the sample surfaces were prepared by mechanically roughening the substrate using an emery paper followed by cleaning in an alkaline bath, maintained at 80 °C, for 15 min. The bath comprised 20 g/L NaCO3, 20 g/L Na2PO4, 20 g/L Na2SiO3, and 3 g/L commercially available OP-10 surfactant. Finally, we rinsed the substrates with DI water before treating them in the PEO baths. Mechanical roughening improved the adhesion between the ceramic coating and the substrate. We ensured that the cleaning step prevented any build-up of the native oxide layer on the substrate.

We treated two sets of Ti-alloys, Ti-A and Ti-B, in a PEO bath consisting of 70 g/L NaOH, 60 g/L Na2SiO3, 10 g/L Na3C6H5O7, 6 mL/L H2O2, and 0.05 milli mol/L sodium dodecyl sulphate. The bath for Sample set ‘B’ contained 4.9 mL/L aminophenol in the bath. We maintained both electrolyte baths at ~ 25 °C. We treated Ti-A and Ti-B samples using a stainless-steel counter electrode for 15 min. A variable DC power supply supplied a constant current of 4 A/dm2 resulting in an average processing voltage of < 120 V.

We used an FEI XL30 equipped with a 30 kV field emission gun to study the surface morphologies and composition of Ti-A and Ti-B coatings. We sputtered the samples with Pt using a Quorum Tech Q150T turbomolecular pumped coater to improve their electron conductivity for SEM imaging.

We collected phase and composition data from Ti-A and Ti-B using a Rigaku XtaLAB Synergy-s single crystal X-ray diffractometer equipped with a Cu Kα source (λ = 1.54184 Å, 2θ = 20° to 80°, 0.02° step size). We used the Materials Explorer application on Materials Project open database40 to index the XRD patterns.

We collected SERS spectra for Ti-A and Ti-B coatings using a WITec alpha300 Raman-AFM spectrometer equipped with a λ = 532 nm Ar-ion laser (− 61 °C). The spectral data was collected using an integration time of 10 s each for five accumulations.

We used a Kratos AXIS DLD X-ray photoelectron spectrometer with a hemispherical electron energy analyser for analysing Ti-A and Ti-B coatings on Ti alloys. We generated the spectra using monochromatic Al Ka X-rays (1486 eV) operated at 150 W. The analysis chamber was at 1 × 10−9 Torr for data collection. We used the survey scans from − 5 to 1350 eV (160 eV pass energy) to determine the material composition. We collected core level data for C, O, Si and Ti for all the samples, and for N from Ti-B samples. We collected the core level data with a pass energy of 20 eV.

We used Casa XPS 2.3.14 to resolve the XPS data by aligning the C 1s peak at 285 eV. We used Thermo Scientific XPS database to analyse the deconvoluted peaks41.

We used a Hysitron TI 950 tribometer equipped with a Berkovich tip to analyse the mechanical behaviour of the ceramic oxide coatings. We applied a maximum load of 1000 mN for 2 s with 5-s preloading and unloading times. We assessed the nanohardness of Ti-A and Ti-B coating cross-sections eliminate any influence of the substrates on the results. We evaluated the nanohardness of untreated control substrates to evaluate the mechanical enhancement provided by the ceramic coating.

We collected diffuse reflectance spectra for Ti-A and T-B coatings using a Shimadzu 2250 UV–Vis spectrophotometer. The photonic energies ranged from 1.5 to 6.2 eV (λ = 200 to 800 nm) with a medium scan speed and 0.016 eV (0.5 nm) resolution. We irradiated the flat samples with a 5° photonic incidence angle via the specular reflectance attachment.

We used a CH Instruments three-cell electrochemical workstation equipped with a Metek designed K0235 flat cell kit to evaluate the electrochemical performance of the oxidized surfaces. Prior to testing, we immersed the samples in 3.5 wt% NaCl solution for 72 h. The tests employed an Ag/AgCl reference electrode and a Pt counter electrode. We collected Tafel data using freshly prepared 3.5 wt% NaCl solution. We determined the open circuit potential (OCP) of Ti-A and Ti-B coatings by scanning them between ± 0.3 V for 5 min. We also performed Electrochemical Impedance Spectroscopy (EIS) applying an AC Voltage of 10 mV amplitude to the OCP, in the range of frequencies tested. An open-source Python package, impedance.py42, was used to analyse the resultant EIS spectra and develop electrochemical equivalent circuits.

Walsh, F. C. et al. Plasma electrolytic oxidation (PEO) for production of anodised coatings on lightweight metal (Al, Mg, Ti) alloys. Trans. IMF 87, 122–135. https://doi.org/10.1179/174591908X372482 (2009).

Article CAS Google Scholar

Sobolev, A., Zinigrad, M. & Borodianskiy, K. Ceramic coating on Ti-6Al-4V by plasma electrolytic oxidation in molten salt: Development and characterization. Surf. Coat. Technol. 408, 10. https://doi.org/10.1016/j.surfcoat.2021.126847 (2021).

Article CAS Google Scholar

Bencina, M., Iglic, A., Mozetic, M. & Junkar, I. Crystallized TiO(2)nanosurfaces in biomedical applications. Nanomaterials 10, 23. https://doi.org/10.3390/nano10061121 (2020).

Article CAS Google Scholar

Zhang, L.-C. & Chen, L.-Y. A review on biomedical titanium alloys: Recent progress and prospect. Adv. Eng. Mater. 21, 1801215. https://doi.org/10.1002/adem.201801215 (2019).

Article CAS Google Scholar

Long, M. & Rack, H. J. Titanium alloys in total joint replacement—A materials science perspective. Biomaterials 19, 1621–1639. https://doi.org/10.1016/s0142-9612(97)00146-4 (1998).

Article CAS PubMed Google Scholar

Zhecheva, A., Sha, W., Malinov, S. & Long, A. Enhancing the microstructure and properties of titanium alloys through nitriding and other surface engineering methods. Surf. Coat. Technol. 200, 2192–2207. https://doi.org/10.1016/j.surfcoat.2004.07.115 (2005).

Article CAS Google Scholar

Cotell, C. M., Sprague, J. A. & Smidt, F. A. Surface Engineering Vol. 5 (ASM International, 1994).

Book Google Scholar

Shibata, H., Tokaji, K., Ogawa, T. & Hori, C. The effect of gas nitriding on fatigue behavior in titanium-alloys. Int. J. Fatigue 16, 370–376. https://doi.org/10.1016/0142-1123(94)90448-0 (1994).

Article CAS Google Scholar

Fujishima, A. & Honda, K. Electrochemical photolysis of water at a semiconductor electrode. Nature 238, 37. https://doi.org/10.1038/238037a0 (1972).

Article ADS CAS PubMed Google Scholar

Hoffmann, M. R., Martin, S. T., Choi, W. Y. & Bahnemann, D. W. Environmental applications of semiconductor photocatalysis. Chem. Rev. 95, 69–96. https://doi.org/10.1021/cr00033a004 (1995).

Article CAS Google Scholar

Uhm, S. H. et al. Tailoring of antibacterial Ag nanostructures on TiO2 nanotube layers by magnetron sputtering. J. Biomed. Mater. Res. B 102, 592–603. https://doi.org/10.1002/jbm.b.33038 (2014).

Article CAS Google Scholar

Jiang, Y. A. et al. Size-controllable Ni5TiO7 nanowires as promising catalysts for CO oxidation. Sci. Rep. 5, 10. https://doi.org/10.1038/srep14330 (2015).

Article CAS Google Scholar

Krumdieck, S. P. et al. Nanostructured TiO2 anatase-rutile-carbon solid coating with visible light antimicrobial activity. Sci. Rep. 9, 11. https://doi.org/10.1038/s41598-018-38291-y (2019).

Article CAS Google Scholar

Zhang, L., Zhang, J., Dai, F. & Han, Y. Cytocompatibility and antibacterial activity of nanostructured H2Ti5O11 center dot H2O outlayered Zn-doped TiO2 coatings on Ti for percutaneous implants. Sci. Rep. 7, 10. https://doi.org/10.1038/s41598-017-13954-4 (2017).

Article ADS CAS Google Scholar

Huang, C. H. & Yoshimura, M. Direct ceramic coating of calcium phosphate doped with strontium via reactive growing integration layer method on alpha-Ti alloy. Sci. Rep. 10, 12. https://doi.org/10.1038/s41598-020-67332-8 (2020).

Article CAS Google Scholar

Fattah-alhosseini, A., Molaei, M. & Babaei, K. The effects of nano- and micro-particles on properties of plasma electrolytic oxidation (PEO) coatings applied on titanium substrates: A review. Surf. Interfaces 21, 20. https://doi.org/10.1016/j.surfin.2020.100659 (2020).

Article CAS Google Scholar

He, T. et al. A comparison of micro-CT and histomorphometry for evaluation of osseointegration of PEO-coated titanium implants in a rat model. Sci. Rep. 7, 11. https://doi.org/10.1038/s41598-017-16465-4 (2017).

Article ADS CAS Google Scholar

Shokouhfar, M. & Allahkaram, S. R. Effect of incorporation of nanoparticles with different composition on wear and corrosion behavior of ceramic coatings developed on pure titanium by micro arc oxidation. Surf. Coat. Technol. 309, 767–778. https://doi.org/10.1016/j.surfcoat.2016.10.089 (2017).

Article CAS Google Scholar

Chen, Z. X. et al. Improving the tribological properties of spark-anodized titanium by magnetron sputtered diamond-like carbon. Coatings 8, 83. https://doi.org/10.3390/coatings8020083 (2018).

Article CAS Google Scholar

Kenna, J. G. A new twist to an old tale: Novel insights into the differential toxicities of acetaminophen and its regioisomer N-acetyl-meta-aminophenol (AMAP). Arch. Toxicol. 87, 15–18. https://doi.org/10.1007/s00204-012-0945-9 (2013).

Article CAS PubMed Google Scholar

Krzakala, A., Kazek-Kesik, A. & Simka, W. Application of plasma electrolytic oxidation to bioactive surface formation on titanium and its alloys. RSC Adv. 3, 19725–19743. https://doi.org/10.1039/c3ra43465f (2013).

Article ADS CAS Google Scholar

Erfanifar, E., Aliofkhazraei, M., Nabavi, H. F. & Rouhaghdam, A. S. Growth kinetics and morphology of microarc oxidation coating on titanium. Surf. Coat. Technol. 315, 567–576. https://doi.org/10.1016/j.surfcoat.2017.03.002 (2017).

Article CAS Google Scholar

Rudnev, V. S. et al. Ta-containing coatings formed on titanium and stainless steel by plasma electrolytic oxidation and/or extraction pyrolysis. Surf. Coat. Technol. 258, 1232–1238. https://doi.org/10.1016/j.surfcoat.2014.06.057 (2014).

Article CAS Google Scholar

Yerokhin, A. L., Nie, X., Leyland, A. & Matthews, A. Characterisation of oxide films produced by plasma electrolytic oxidation of a Ti-6Al-4V alloy. Surf. Coat. Technol. 130, 195–206. https://doi.org/10.1016/s0257-8972(00)00719-2 (2000).

Article CAS Google Scholar

Gracia, L., Beltran, A. & Errandonea, D. Characterization of the TiSiO4 structure and its pressure-induced phase transformations: Density functional theory study. Phys. Rev. B 80, 10. https://doi.org/10.1103/PhysRevB.80.094105 (2009).

Article CAS Google Scholar

Zhang, L. H. & Koka, R. V. A study on the oxidation and carbon diffusion of TiC in alumina titanium carbide ceramics using XPS and Raman spectroscopy. Mater. Chem. Phys. 57, 23–32. https://doi.org/10.1016/s0254-0584(98)00187-4 (1998).

Article CAS Google Scholar

Kong, F. Y., Gu, S. X., Wang, J. Y., Fang, H. L. & Wang, W. Facile green synthesis of graphene-titanium nitride hybrid nanostructure for the simultaneous determination of acetaminophen and 4-aminophenol. Sens. Actuator B Chem. 213, 397–403. https://doi.org/10.1016/j.snb.2015.02.120 (2015).

Article CAS Google Scholar

Peng, T., Kou, Z., Wu, H. & Mu, S. Graphene from amorphous titanium carbide by chlorination under 200 °C and atmospheric pressures. Sci. Rep. 4, 5494. https://doi.org/10.1038/srep05494 (2014).

Article ADS CAS PubMed PubMed Central Google Scholar

Aliofkhazraei, M. et al. Review of plasma electrolytic oxidation of titanium substrates: Mechanism, properties, applications and limitations. Appl. Surf. Sci. Adv. 5, 67. https://doi.org/10.1016/j.apsadv.2021.100121 (2021).

Article Google Scholar

Arslan, E., Totik, Y., Demirci, E. E. & Efeoglu, I. Wear and adhesion resistance of duplex coatings deposited on Ti6Al4V alloy using MAO and CFUBMS. Surf. Coat. Technol. 214, 1–7. https://doi.org/10.1016/j.surfcoat.2012.10.006 (2013).

Article CAS Google Scholar

Ming, S. L. et al. Fabrication and characterization of porous micro-arc oxidation/Al composite coating: Bio-inspired strategy from cancellous bone structure. J. Mater. Eng. Perform. 29, 87–97. https://doi.org/10.1007/s11665-019-04533-x (2020).

Article CAS Google Scholar

Schirdewahn, S., Spranger, F., Hilgenberg, K. & Merklein, M. Localized laser dispersing of titanium-based particles for improving the tribological performance of hot stamping tools. J. Manuf. Mater. Process. 4, 19. https://doi.org/10.3390/jmmp4030068 (2020).

Article CAS Google Scholar

Asahi, R., Morikawa, T., Ohwaki, T., Aoki, K. & Taga, Y. Visible-light photocatalysis in nitrogen-doped titanium oxides. Science 293, 269–271. https://doi.org/10.1126/science.1061051 (2001).

Article CAS PubMed Google Scholar

Leary, R. & Westwood, A. Carbonaceous nanomaterials for the enhancement of TiO2 photocatalysis. Carbon 49, 741–772. https://doi.org/10.1016/j.carbon.2010.10.010 (2011).

Article CAS Google Scholar

Hoche, H. et al. Investigation of the macroscopic and microscopic electrochemical corrosion behaviour of PVD-coated magnesium die cast alloy AZ91. Surf. Coat. Technol. 193, 178–184. https://doi.org/10.1016/j.surfcoat.2004.08.204 (2005).

Article CAS Google Scholar

Galvis, O. A. et al. Formation of grooved and porous coatings on titanium by plasma electrolytic oxidation in H2SO4/H3PO4 electrolytes and effects of coating morphology on adhesive bonding. Surf. Coat. Technol. 269, 238–249. https://doi.org/10.1016/j.surfcoat.2015.02.036 (2015).

Article CAS Google Scholar

Shen, W. & Fan, W. Nitrogen-containing porous carbons: Synthesis and application. J. Mater. Chem. A 1, 999–1013. https://doi.org/10.1039/C2TA00028H (2013).

Article CAS Google Scholar

Lin, G. W., Huang, Y. H., Tseng, W. J. & Lu, F. H. Production of N-doped anatase TiO2 on TiN-coated Ti substrates by plasma electrolytic oxidation for visible-light photocatalysts. Ceram. Int. 45, 22506–22512. https://doi.org/10.1016/j.ceramint.2019.07.275 (2019).

Article CAS Google Scholar

Tao, W. et al. Multi-layered porous hierarchical TiO2/g-C3N4 hybrid coating for enhanced visible light photocatalysis. Appl. Surf. Sci. 495, 8. https://doi.org/10.1016/j.apsusc.2019.07.177 (2019).

Article CAS Google Scholar

Jain, A. et al. Commentary: The materials project: A materials genome approach to accelerating materials innovation. APL Mater. 1, 011002. https://doi.org/10.1063/1.4812323 (2013).

Article ADS CAS Google Scholar

Thermo Fisher Scientific. XPS Simplified/Elements Table. https://xpssimplified.com/periodictable.php (2020). Accessed 18 August 2021.

Murbach, M. D., Gerwe, B., Dawson-Elli, N. & Tsui, L.-K. Impedance.py: A python package for electrochemical impedance analysis. J. Open Source Softw. 5, 2349 (2020).

Article ADS Google Scholar

Download references

We thank Catherine Hobbis and Colin Doyle of Research Centre for Surface and Materials Science at The University of Auckland (UoA). We also thank Tianping Zhu for assisting with potentiodynamic testing of the coatings. We are grateful to Prof. Wei Gao for providing us with access to the characterization facilities at UoA. This work received partial funding from Callaghan Innovation.

Cirrus Materials Science Ltd., 5B Target Ct., Auckland, 0627, New Zealand

Fengyan Hou, Rukmini Gorthy, Ian Mardon, Da Tang & Chris Goode

Department of Chemical and Materials Engineering, The University of Auckland, 20 Symonds Street, Auckland, 1010, New Zealand

Da Tang

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

F.H., R.G., I.M., C.G., are the lead authors. F.H. is the inventor of the modified PEO process. F.H., R.G., D.T., conducted the materials characterization and testing. I.M. performed the analysis on potentiodynamic test results. F.H., R.G., I.M., C.G., conducted literature review and discussed the results.

Correspondence to Rukmini Gorthy.

The authors declare no competing interests. The authors are employees of Cirrus Materials Science Ltd. The copyright belongs to Cirrus Materials Science Ltd. © Cirrus Materials Science Ltd. 2022

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Hou, F., Gorthy, R., Mardon, I. et al. Low voltage environmentally friendly plasma electrolytic oxidation process for titanium alloys. Sci Rep 12, 6037 (2022). https://doi.org/10.1038/s41598-022-09693-w

Download citation

Received: 07 September 2021

Accepted: 23 March 2022

Published: 11 April 2022

DOI: https://doi.org/10.1038/s41598-022-09693-w

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.