Morphology of subsurface cracks in glass

Dec 06, 2023

Scientific Reports volume 12, Article number: 6994 (2022) Cite this article

1516 Accesses

11 Citations

1 Altmetric

Metrics details

The characterization of subsurface cracks induced by indentation is a challenge for understanding contact damage, impact, wear, erosion, and abrasion of brittle materials, because the crack pattern observable on the surface is only a part of the total crack system. Here we applied synchrotron X-ray multiscale tomography to observe the morphology of subsurface cracks produced by Vickers indentation in a novel CaO–Al2O3–SiO2 glass-ceramic with plate-like crystals forming a house-of-cards microstructure. It revealed a diverse type of crack systems around the semispherical microcrack zone beneath the indent, including a new mode II inclined lateral crack driven by the maximum shear stress. Tomography images provided knowledge on how the heterogeneous microstructure affected the toughening processes such as crack deflection, crack bridging, and microcracking.

Crack patterns on the surface induced by sharp or blunt indenter provide rich knowledge on mechanical properties of brittle materials, such as glass, glass-ceramic, ceramics, and composites, for developing damage resistant materials in structural, dental and optical applications. Vickers indenter generates radial1,2, median1,2, and lateral cracks1,3, which initiate at the boundary of elastic–plastic deformation zone, or, process zone. The driving force of crack formation is the maximum principal stress around the elastic–plastic deformation zone4; \(\sigma_{\phi \phi }\) on the surface (\(\theta = \pi /2\)) for radial crack, \(\sigma_{\theta \theta }\) at the bottom of process zone (\(\theta = 0\)) for median crack, and \(\sigma_{rr}\) (\(\theta = 0\)) for lateral crack, where \(\theta\) is the angle to the loading axis in spherical polar coordinates, \(\phi\) is the hoop angle about the loading axis, and r is the radial distance. The initiation and growth of cracks in transparent materials are observed directly by optical microscopy under loading and unloading sequences5. The crack pattern depends on the local deformation behavior in the process zone, for example, densification and shear flow in glass6,7. The 3D crack system will be more complex in tough materials having heterogeneous microstructure with weak internal interfaces and high internal residual stress. Spherical indenter leads to Hertzian cone crack or subsurface deformation zone beneath the contact8. This microcrack damage zone is associated with nonlinear stress–strain curves, or quasi-plasticity9, in mica glass-ceramic10 and heterogeneous ceramics.

The complicated subsurface indentation crack system has been studied by observing the cross-section using optical microscopy8,11,12 and scanning electron microscopy (SEM)13,14. Focused ion beam (FIB) tomography can be used as a serial sectioning technique15,16. However, these sectioning methods affect the stress field around the process zone, so that it may alter the original morphology of crack system. X-ray computed tomography (CT) is a powerful technique to observe the internal cracks non-destructively17. Lacondemine et al.18 performed in-situ Vickers indentation experiment by means of X-ray tomography, and assessed the displacement field using a Digital Volume Correlation routine (DVC). Okuma19 clearly detected crack-like defects formed during powder processing and sintering of alumina by using a multiscale X-ray computed tomography, which was developed by Takeuchi and co-workers in SPring-820,21.

The purpose of this work is to investigate the complicated 3D crack system generated in brittle materials with heterogeneous microstructure by using the multiscale X-ray computed tomography. Here, we used a translucent glass-ceramic as a model material. The glass-ceramics are defined as inorganic, non-metallic materials prepared by controlled crystallization of glasses via different processing methods22,23. A wide variety of glass-ceramic with heterogeneous microstructures have been developed by controlling the chemical composition of glass and the size, shape, and volume fraction of crystalline phase embedded in the glass for improving strength and fracture toughness24,25,26. The residual stresses that arise from thermal expansion and elastic mismatch between the crystal and the glass affect the mechanical properties of glass-ceramic27. The possible toughening mechanisms applicable to glass-ceramic are crack bowing28, crack deflection28,29, crack bridging30,31, and microcrack toughening32,33. A novel glass-ceramic composed of a CaO–Al2O3–SiO2 glass and hexagonal CaAl2Si2O8 crystals (h-CAS) was found by Maeda34,35 recently. This glass-ceramic (CAS-GC) exhibited improved fracture toughness and non-linear load–displacement curves in bending tests using the Single Edge V-Notched Beam (SEVNB) specimens34,36. The crack propagation is influenced by a house-of-cards microstructure formed by plate-like h-CAS crystals36,37. Cracks travel along the glass-crystal interface and the cleavage plane, since the h-CAS crystal structure is analogous to that of mica38. The CAS-GC is highly resistant to the abrasion damage39. We investigated 3D crack structure induced by Vickers indentation in CAS-GC by using the multiscale X-ray computed tomography. An attempt was made to understand the complicated subsurface crack system as a collection of crack components.

Figure 1 shows Vickers indentation crack patterns for various loads in translucent CAS-GC observed by optical microscopy. The indentation cracks are symmetric at high loads, 196 N and 98 N, as schematically illustrated in Fig. 1a. The subsurface lateral crack is seen as a brilliant circular area (Fig. 1b,c), in contrast to smooth lateral cracks observed in glasses (Supplementary Fig. S1). Four radial cracks on the surface emanate from corners of the indent. The microcrack zone is defined as a circular opaque white area at the center (dashed line in Fig. 1c). The lateral crack system is composed of four circular sectors, the shape and size of which are irregular at loads less than or equal to 29.4 N (Fig. 1d,e). The radii of radial crack c, lateral crack r, microcrack zone R, and indent size a increase with indentation load P according to power law relationship

where L represents the radii and n is an exponent (Supplementary Fig. S2). The exponents for radial crack and lateral crack were 0.57 and 0.65, respectively. They were approximately equal to the theoretical value of 2/3 for radial crack2 and 5/8 for lateral crack3. The exponent of 0.73 for microcrack zone was closer to the value of 0.57 for radial and 0.66 for lateral crack systems than the value of 0.5 for indent size.

Optical micrograph of cracks induced by Vickers indentation in CaO–Al2O3–SiO2 glass-ceramic (CAS-GC). (a) An idealized crack structure, (b) indentation load 196 N, (c) 98 N, (d) 29.4 N, (e) 9.8 N.

Figure 2a represents the top view of micro-CT image of a CAS-GC specimen indented at 29.4 N load (see also Supplementary Movie 1). Ring artifacts appear as circles centered on the axis of rotation of the sample during data acquisition. There were four primary radial cracks (R1–R4), two of them accompanying secondary radial cracks (SR1, SR2) which emanated adjacent to indentation corners. Three asymmetric shallow lateral cracks (L1, L2, L3) had irregular shapes. The shallow lateral crack (L1) was bounded by a secondary radial crack (SR1). The secondary radial crack (SR2) inclined to the loading axis. The side view in Fig. 2b showed the semispherical microcrack zone. The radial/median crack system looked like a so-called half-penny crack with annular geometry, because both radial crack and median crack initiated near the boundary of the microcrack zone and extended outward. However, radial cracks R1, SR1, R3 were not actually connected in the region below the microcrack zone. The cross-sections along lines (i) and (ii) in Fig. 2a are illustrated in Fig. 2c, indicating shallow lateral cracks (L1 and L3) parallel to the surface and a median crack perpendicular to it. This median crack was connected with radial crack R4. The microcrack zone or the damage zone in the semicircle (dashed line in Fig. 2c) contained numerous small dark spots, which corresponded microcracks. The shallow lateral cracks initiated inside the microcrack zone.

Micro-CT observation of Vickers indentation cracks at 29.4 N load. (a) Top view, (b) side view, (c) 2D cross-sectional image along white dashed lines (i) and (ii) in (a).

The subsurface crack system was divided into three layers in Fig. 3; (a) upper layer, (b) middle layer, and (c) lower layer. The shallow lateral cracks located in the upper layer near the surface (Fig. 3a). The topography of the surface of shallow lateral crack was rough and wavy, as shown in Supplementary Fig. S3 in detail. The rough surface is the origin of the brilliant appearance of lateral cracks of CAS-GC observed by optical microscopy. The rough crack surface has been attributed to crack deflection by plate-like CAS crystals, which form a house-of-cards structure36. The evidence of crack deflection was seen not only for lateral cracks, but also for median crack from the crack profiles presented in Fig. 2c. The middle layer (Fig. 3b) indicates the circular microcrack zone at the center and radial cracks outside the zone. In the lower layer below the microcrack zone (Fig. 3c), there was only one median crack, which was connected with radial crack R4. The connection between the median crack and radial cracks R2 and SR2 was not detected unambiguously. There was no median crack, which connected radial cracks R1 and R3. As Cook and Pharr5 pointed out, cracks emanating from the indentation corners are not always originated from the median cracks. Figure 4a illustrates the schematic representation of crack system by Vickers indentation around the indent and the semi spherical process zone.

Layer structure of subsurface cracks induced by Vickers indentation at 29.4 N load. (a) Upper layer, (b) middle layer, (c) lower layer. Shallow lateral cracks (L1, L2, and L3) located in the upper layer near the surface. The middle layer indicates the circular microcrack zone at the center and radial cracks outside the zone. There was only one median crack in the lower layer below the microcrack zone.

Schematic illustration of crack system induced by Vickers indentation around the indent and the semispherical process zone. (a) A crack model for loading at 29.4 N. Radial crack (R), secondary radial crack (SR), Palmqvist crack (Pq), lateral crack (L). Coordination system used to define the stress field at an indentation contact is illustrated. (b) Geometry of an inclined crack.

The indentation crack patterns become irregular under low loading, because the crack nucleation is affected by the microstructural heterogeneity. We observed carefully the complicated crack structure at 9.8 N load by using micro- and nano-CT [see Supplementary Movies 2 (micro-CT) and 3 (nano-CT)]. The top view and the side view of micro-CT image of the cracks are shown in Fig. 5a,b, respectively. They reveal that a diversity of cracks with different types, locations, and orientations, are formed outside the microcrack zone. Some complicated crack systems, (SL + IL) and (IL1 + IL2) in Fig. 5a observed by micro-CT, are considered as combined cracks consisting of several components as illustrated in Fig. 6a,b, respectively. The inclined lateral crack was identified as a new type of crack component. The inclined lateral crack (IL) initiates along a shallow lateral crack (SL) (Fig. 6a) or a surface-localized radial crack (Palmqvist crack, Pq) (Fig. 6b). The orientation of inclined lateral crack was different from that of radial crack and median crack (parallel to the load axis) or lateral crack (perpendicular to the load axis). While a shallow lateral crack5 propagates almost parallel to the surface, the inclined lateral crack goes into surrounding material at an angle to the load axis in a similar way to the secondary radial crack (SR2 in Fig. 4a). The orientation of the inclined lateral crack suggests a mode II crack driven by shear stress. Yoffe4 proposed that the stress field around the elastic–plastic deformation zone was given as the superposition of a point-contact field (Boussinesq field) and a blister field due to the permanent deformation beneath the indenter. The coordinate system used to describe the stress field is illustrated in Fig. 4a. Both Boussinesq field and blister field have the maximum shear stress \(\tau_{r\theta }\) at \(\theta = \pi /4\), then, this shear stress may affect the initiation and propagation of a mode II crack in the middle layer between the surface and the bottom of the process zone. The geometry of an inclined crack is defined by the initiation location (the depth d from the surface and the angle \(\psi\)) and the orientation \({\Theta }\) of the crack as shown in Fig. 4b; for example, \(d > 0\), \(\pi /2 >\Theta > \pi /4\) for inclined lateral crack, \(d = 0\), \(\psi > 0,\) \(\pi /4 >\Theta > 0\) for secondary radial crack, \(d = 0\), \(\psi = 0,\) \({\Theta } = 0\) for radial crack, \(d > 0\), \(\Theta = \pi /2\) for lateral crack, and \(d > R\), \(\Theta = 0\) for median crack. Xie et al.14 and Baggott et al.16 reported lateral cracks interconnecting with radial crack beneath Vickers indentation on silicon nitride. Such crack structure can be also regarded as a combined crack system consisting of a radial crack and two inclined lateral cracks.

Micro-CT and nano-CT observation of Vickers indentation cracks at 9.8 N load. (a) Top view and (b) side view of micro-CT image. (c) and (d) side view of a region-of-interest [ROI, a cube shown as squares in (a) and (b)] observed by nano-CT. Arrows in (a) indicate the relative orientation of panels (b), (c), and (d). (SL: Shallow lateral crack, SR: Secondary radial crack, IL: Inclined lateral crack, M: Median crack, S: Single rectangular crack).

Components of indentation crack system. (a) Combined crack consisting of a shallow lateral crack (SL) and an inclined lateral crack (IL) in Fig. 5a, (b) combined crack consisting of a surface localized radial crack (Palmqvist crack, Pq) and two inclined lateral cracks (IL1, IL2) in Fig. 5a, (c) secondary radial crack (SR) in Fig. 5a,b, (d) parallel ribbon-like cracks in Fig. 5c (red arrows), (e) the house-of-cards structure of h-CAS crystals observed by FIB-SEM tomography, (f) two rectangular holes on secondary radial crack (SR) in Fig. 5d and a crack bridging model of a platelet located parallel to crack surface.

Micro-CT in Fig. 5b could detect only a part of crack surface with large crack opening displacement (COD), so that it gave the appearance of a collection of porous fragments. High resolution nano-CT observation was conducted to investigate the lower part of the microcrack zone and cracks formed outside the zone boundary (the region inside red squares in Fig. 5a,b). The side view of the region observed by nano-CT revealed the detailed crack structure. The inclined lateral crack (IL1) in Fig. 5c,d is a component of combined crack in Fig. 6b, which initiated below a Palmqvist crack (\(R > d > 0\)). The topography of the inclined lateral crack was rough and wavy in a similar way to the shallow lateral crack (Supplementary Fig. S3). An inclined lateral crack (IL3 in Fig. 5d) was also initiated in a region below the microcrack zone (\(d > R\)). On the other hand, a significant crack deflection and crack branching were observed in the secondary radial crack (SR) in Figs. 5c,d and 6c. There were several rectangular cracks (S1, S2, and S3). They looked like cracks at the interface between a single plate-like CAS crystal and glass matrix or cleavage plane, which initiated independently. The red arrows in Fig. 5c indicate a series of parallel cracks like ribbon strips. The enlarged view is illustrated in Fig. 6d. This crack structure is also related to a single rectangular h-CAS crystal. The house-of-cards structure was observed by FIB-SEM tomography37, and presented in Fig. 6e. The surface of platelet was not flat perfectly, but there were surface undulations due to the instability during crystal growth. The parallel cracks are localized microcracks at the interface generated by stress concentrations along the surface undulations.

The median cracks (M1–M5) were formed in the region below the microcrack zone (Fig. 5c,d). They are flat and parallel to the load axis. This is the region where two median cracks should be nucleated usually bisecting each other at right angles in the ideal model. However, the observed crack was a connected series of flat cracks. It suggested that multiple nucleation of median cracks occurred due to the house-of-cards structure in CAS-GC. The structure of median crack system was observed in the cross-section perpendicular to the loading axis at the position indicated by white dashed line in Fig. 5c,d. Although median cracks could be detected by micro-CT (Fig. 7a), the apparent COD was about 1.5–2 µm as the spatial resolution is typically 2–3 times the voxel size (0.5 µm). Nano-CT observation indicated that the actual size of COD was 0.5 µm (Fig. 7b).

Median cracks. (a) Cross sectional image of median cracks observed by micro-CT, (b) Cross sectional image of median cracks observed by nano-CT.

The high fracture toughness of the CAS-GC (KIC = 2.22 MPa m1/2 by SEVNB method) is attributed to crack deflection mechanism28,29. The fracture surface of CAS-GC after bending test was rough34,36 and consisted of flat facets indicating crack propagation along the interface between h-CAS crystals and glass or cleavage plane, because h-CAS crystal is analogous to mica37,38. The rough fracture surface was correlated with the house-of-cards structure34,36. The crack deflection of the secondary radial crack (SR1 in Figs. 5d, 6c) agreed with previous studies. On the other hand, the wavy profiles of lateral crack and inclined lateral crack (IL1 in Fig. 5c) indicate that the crack can propagates within the glass matrix and penetrate into h-CAS crystals, in addition to crack deflection28,29. Furthermore, the median cracks were quite flat. The observed diversity in crack profile suggests that the crack deflection depends on the crack type, the fracture mode, and the local stress field.

Two rectangular holes were observed on the surface of secondary radial crack (SR) in Fig. 5d (inside a rectangle). The holes locate on a crack surface with terrace-and-step morphology (Fig. 6f). This structure is related to the presence of rectangular h-CAS crystal on the crack surface as schematically illustrated in Fig. 6f. The upper part of the crack surface is partly bonded to the lower part via the h-CAS crystal. The toughening theory on crack bridging usually assumes reinforcements, fiber30,31 or platelets40, vertically located on the crack surface. The present observation showed that platelets parallel to the crack surface can contribute to the toughening by crack bridging.

The formation of microcrack zone by Vickers indentation was imaged by using micro-CT in CAS-GC with heterogeneous microstructure. Lawn8 reviewed that such damage zone, or quasi-plastic zone had been induced also in glass-ceramics and ceramics with heterogeneous microstructures beneath spherical indenters, in the region where the shear stress was maximum. The boundary of damage zone was determined by the shear stress contour. In the subsurface damage zone of mica glass-ceramics, shear-fault micro-failures ("closed" mode II cracks) occurred at weak interfaces between mica platelets and glass phase9. Lawn presented a model that the formation and the sliding at the shear fault would produce "wing" cracks on both sides of the shear fault at high loads. In CAS-GC, the shear stress would cause a fault along h-CAS crystal in the microcrack zone. The shear-fault/wing-crack system may be created at high loads as schematically illustrated in Fig. 8a,b. The crack opening displacement of the wing crack will be the maximum along the edge of h-CAS crystal. However, such wing-crack system could not be observed by nano-CT in microcrack zone formed under the load of 9.8 N (Fig. 8c). There were several ribbon-like cracks which resemble the localized microcracks at the interface of h-CAS crystal (Fig. 6d). As the surface of h-CAS crystal is modulated, ribbon-like cracks will be formed by shear stress (Fig. 8b). The micro-CT image of the microcrack zone induced by Vickers indentation at load of 29.4 N revealed the presence of rod-like defects, some of which were parallel (Fig. 8d). It is supposed that parallel ribbon-like cracks on the interface of platelets are observed as rod-like defects due to the resolution limit of micro-CT.

Ribbon-like crack/wing-crack models in the microcrack zone. (a) Damage zone under Vickers indenter, (b) formation of ribbon-like cracks on the modulated surface and that of wing-cracks on both sides of a flat surface of an individual plate-like crystal, (c) nano-CT image of the microcrack zone induced by Vickers indentation at 9.8 N, (d) micro-CT image of the microcrack zone induced by Vickers indentation at 29.4 N. Some rod-like defects are parallel.

Fu and Evans32,33 analyzed the formation of microcrack around a primary crack, and proposed microcrack toughening. The microcracking reduces the elastic modulus of microcrack process zone, thereby, mitigating the stress field around the primary crack. Microcracking in heterogeneous glass-ceramics is assisted by the internal residual stress27, which arise during cooling due to the difference in thermal expansion and elastic constants. However, we could not detect such microcrack process zone around the median cracks by using nano-CT, although there were a few microcracks. The high fracture toughness of CAS-GC cannot be explained by microcrack toughening but by crack deflection and crack bowing.

The indentation crack pattern becomes symmetric with increasing load, because cracks can initiate at the maximum principal stress as the number of available crack nucleation site increases. The crack pattern is irregular at low load, since the crack initiation depends on the heterogeneous distribution of CAS crystals as the available nucleation sites decrease. Therefore, new type of inclined crack (Fig. 4b) was formed when the crack nucleated at irregular site. Supplementary Fig. S4 indicates the early stage of crack initiation at very small load (400 mN)37. The cracks initiate along the cleavage plane of CAS crystal or the interface between crystal phase and glass stochastically.

In summary, we investigated the complex morphology of subsurface cracking induced by Vickers indentation in a glass ceramic with heterogeneous microstructure by using synchrotron X-ray multiscale tomography. The details of crack shape could be imaged by nano-CT, while the overall structure of complex crack system was observed by micro-CT. The complicated crack morphology arose due to the stochastic nature of crack nucleation in the inhomogeneous microstructure. Some crack systems were expressed as combined crack consisting of several components. The knowledge of subsurface crack morphology, which can never be observed on the surface, are required as a sound basis for characterizing the mechanical behaviors by indentation technique41,42. The multiscale tomography provides an opportunity to investigate the diversity of subsurface crack morphology in toughened materials with heterogeneous microstructures, glass ceramic, ceramics, hard metals and composites, systematically.

The precursor glass composition of 25CaO–20Al2O3–55SiO2 wt% was selected considering the low-liquidus temperature with an adequate viscosity. The precursor glass was prepared from related raw materials by melting at 1550 °C. For promoting crystallization, small amount of MoO3 was added into the mixture of the raw materials. MoO3 was reduced to metallic state during melting or heat treatment process by co-added reducing agents, and served as a nucleating agent of the hexagonal CaAl2Si2O8 crystals43. For the sample of X-ray tomography observation, 0.05 wt% of MoO3 and 0.4 wt% of carbon powder were added, whereas 0.005 wt% of MoO3, 0.4 wt% of carbon powder, and 0.28 wt% of TiO2 were added in case of the sample for optical microscopy observation shown in Fig. 1. The glass sample was heat treated at 1050 °C for 2 h for crystallization32. This glass ceramic (CAS-GC) contained ~ 21 wt% hexagonal CaAl2Si2O8 crystals with sizes less than 10–20 µm and the thickness of ~ 1 µm. The plate-like crystals formed a house-of-cards structure35. For X-ray tomography, cylindrical samples with 0.85 mm in diameter and 7 mm in length were fabricated from the bulk CAS-GC. Vickers indentation was carried out on the polished top surface of samples which were bundled by resin as illustrated in Supplementary Fig. S5. The indentation was performed using Vickers hardness tester (Matsuzawa Via, Akita, Japan) at loads of 9.8 N and 29.4 N. These loads were selected, because the cylindrical sample was broken at 49 N load.

The 3D structure of subsurface cracks was studied by using the synchrotron X-ray multiscale-CT consisting of a micro-CT (microtomography) as a wide-field and low-resolution system and a nano-CT (nanotomography) as a narrow-field and high-resolution system at BL20XU of the Japanese synchrotron radiation facility, SPring-819,20. X-ray energy was set at 20 keV for micro- and nano-CT mode. Optical system of nano-CT mode was based on a phase contrast X-ray full-field microscope. A hollow-cone illumination system using a condenser zone plate (CZP), sample stages, a Fresnel zone plate (FZP) objective, and a Zernike phase plate (phase ring) were placed at the experimental hutch 1. A visible-light conversion type X-ray image detector (C12849-SY69701, Hamamatsu Photonics, Shizuoka, Japan) was installed at the 2nd hutch located ~ 160 m downstream from the 1st hutch. The sample was rotated by steps of 0.1° up to 180°. Voxel sizes for micro- and nano-CT mode were 0.5 μm and 40 nm, respectively. The measuring time for one sample was ∼8 min and ∼30 min for micro- and nano-CT, respectively. The micro-CT is used to capture the entire structure of indentation cracks, and its region-of-interest (ROI) is measured with nano-CT precisely.

The images were reconstructed from the acquired data by using a filtered back-projection method. Gaussian filtering was applied to reduce the noise in 2D images. The 3D visualization and geometrical measurements were performed using Amira (VSG, Burlington, Massachusetts, USA) and Dragonfly (Object Research Systems (ORS) Inc.). Local thresholding method was used to segment the gray value image into crack and material. The surface was discretized using triangular meshing.

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Lawn, B. & Wilshaw, R. Indentation fracture: Principles and applications. J. Mater. Sci. 10, 1049–1081 (1975).

Article ADS Google Scholar

Lawn, B. R., Evans, A. G. & Marshall, D. B. Elastic/plastic indentation damage in ceramics: The median/radial crack system. J. Am. Ceram. Soc. 63, 574–581 (1980).

Article CAS Google Scholar

Marshall, D. B., Lawn, B. R. & Evans, A. G. Elastic/plastic indentation damage in ceramics: The lateral crack system. J. Am. Ceram. Soc. 65, 561–566 (1982).

Article CAS Google Scholar

Yoffe, E. H. Elastic stress fields caused by indenting brittle materials. Philos Mag A 46, 617–628 (1982).

Article ADS CAS Google Scholar

Cook, R. F. & Pharr, G. M. Direct observation and analysis of indentation cracking in glasses and ceramics. J. Am. Ceram. Soc. 73, 787–817 (1990).

Article CAS Google Scholar

Rouxel, T. Driving force for indentation cracking in glass: Composition, pressure and temperature dependence. Philos. Trans. R. Soc. A 373, 20140140 (2015).

Article ADS CAS Google Scholar

Yoshida, S. Indentation deformation and cracking in oxide glass–toward understanding of crack nucleation. J. Non-Cryst. Solids X 1, 100009 (2019).

CAS Google Scholar

Lawn, B. R. Indentation of ceramics with spheres: A century after Hertz. J. Am. Ceram. Soc. 81, 1977–1994 (1998).

Article CAS Google Scholar

Lawn, B. R., Padture, N. P., Cai, H. & Guiberteau, F. Making ceramics ductile. Science 263, 1114–1116 (1994).

Article ADS CAS PubMed Google Scholar

Peterson, I. M., Wuttiphan, S., Lawn, B. R. & Chyung, K. Role of microstructure on contact damage and strength degradation of micaceous glass-ceramics. Dent. Mater. 14, 80–89 (1998).

Article CAS PubMed Google Scholar

Arora, A., Marshall, D. B., Lawn, B. R. & Swain, M. V. Indentation deformation/fracture of normal and anomalous glasses. J. Non-Cryst. Solids. 31, 415–428 (1979).

Article ADS CAS Google Scholar

Whittle, B. R. & Hand, R. J. Morphology of vickers indent flaws in soda–lime–silica glass. J. Am. Ceram. Soc. 84, 2361–2365 (2001).

Article CAS Google Scholar

Lube, T. Indentation crack profiles in silicon nitride. J. Eur. Ceram. Soc. 21, 211–218 (2001).

Article CAS Google Scholar

Xie, Z.-H., Hoffman, M., Moon, R. J. & Munroe, P. R. Subsurface indentation damage and mechanical characterization of a-sialon ceramics. J. Am. Ceram. Soc. 87, 2114–2124 (2004).

Article CAS Google Scholar

Cuadrado, N., Seuba, J., Casellas, D., Anglada, M. & Jiménez-Piqué, E. Geometry of nanoindentation cube-corner cracks observed by FIB tomography: Implication for fracture resistance estimation. J. Eur. Ceram. Soc. 35, 2949–2955 (2015).

Article CAS Google Scholar

Baggott, A., Mazaheri, M. & Inkson, B. J. 3D characterisation of indentation induced sub-surface cracking in silicon nitride using FIB tomography. J. Eur. Ceram. Soc. 39, 3620–3626 (2019).

Article CAS Google Scholar

Wu, S. C., Xiao, T. Q. & Withers, P. J. The imaging of failure in structural materials by synchrotron radiation X-ray microtomograpjy. Eng. Fract. Mech. 182, 127–156 (2017).

Article Google Scholar

Lacondemine, T. et al. Direct observation of the displacement field and microcracking in a glass by means of X-ray tomography during in situ Vickers indentation experiment. Acta Mater. 179, 424–433 (2019).

Article ADS CAS Google Scholar

Okuma, G. et al. 3D multiscale-imaging of processing-induced defects formed during sintering of hierarchical powder packings. Sci. Rep. 9, 11595 (2019).

Article ADS PubMed PubMed Central CAS Google Scholar

Takeuchi, A., Uesugi, K., Uesugi, M., Yoshinaka, F. & Nakamura, T. Nondestructive multiscale X-ray tomography by combining microtomography and high-energy phase-contrast nanotomography. Microsc. Microanal. 24, 106–107 (2018).

Google Scholar

Takeuchi, A. et al. High-energy X-ray nanotomography introducing an apodization Fresnel zone plate objective lens. Rev. Sci. Instrum 92, 023701 (2021).

Article ADS CAS PubMed Google Scholar

Holland, W. & Beall, G. H. Glass-Ceramic Technology 3rd edn. (American Ceramic Society, Hoboken, 2019).

Book Google Scholar

Deubener, J. et al. Updated definition of glass-ceramics. J. Non-Cryst. Solids. 501, 3–10 (2018).

Article ADS CAS Google Scholar

Fu, Q., Beall, G. H. & Smith, C. M. Nature-inspired design of strong, tough glass-ceramics. MRS Bull. 42, 220–225 (2017).

Article ADS CAS Google Scholar

Apel, E. et al. Phenomena and mechanisms of crack propagation in glass ceramics. J. Mech. Behav. Biomed. Mater. 1, 313–325 (2008).

Article CAS PubMed Google Scholar

Serbena, F. C., Mathias, I., Foerstera, C. E. & Zanotto, E. D. Crystallization toughening of a model glass-ceramic. Acta Mater. 86, 216–228 (2015).

Article ADS CAS Google Scholar

Serbena, F. C. & Zanotto, E. D. Internal residual stresses in glass-ceramics: A review. J. Non-Cryst. Solids 358, 975–984 (2012).

Article ADS CAS Google Scholar

Faber, K. T. & Evans, A. G. Crack deflection process—I. Theory. Acta Metall. 31, 565–576 (1983).

Article Google Scholar

Faber, K. T. & Evans, A. G. Crack deflection process—II. Experiment. Acta Metall. 31, 577–584 (1983).

Article Google Scholar

Marshall, D. B. & Evans, A. G. Failure mechanisms in ceramic-fiber/ceramic-matrix composites. J. Am. Ceram. Soc. 68, 225–231 (1985).

Article CAS Google Scholar

Becher, P. F. Microstructural design of toughened ceramics. J. Am. Ceram. Soc. 74, 255–269 (1991).

Article CAS Google Scholar

Fu, Y. & Evans, A. G. Microcrack zone formation in single phase polycrystals. Acta Metall. 30, 1619–1625 (1982).

Article Google Scholar

Evans, A. G. & Fu, Y. Some effects of microcracks on the mechanical properties of brittle solids—II. Microcrack toughening. Acta Metall. 33, 1525–1531 (1985).

Article Google Scholar

Maeda, K. & Yasumori, A. Toughening of CaO–Al2O3–SiO2 glass by dmisteinbergite precipitation. Mater. Lett. 180, 231–234 (2016).

Article CAS Google Scholar

Maeda, K., Akatsuka, K., Okuma, G. & Yasumori, A. Mechanical properties of CaO–Al2O3–SiO2 glass-ceramics precipitating hexagonal CaAl2Si2O8. Curr. Comput.-Aided Drug Des. 11, 393 (2021).

CAS Google Scholar

Inage, K. et al. Effect of crystallinity and microstructure on mechanical properties of CaO–Al2O3–SiO2 glass toughened by precipitation of hexagonal CaAl2Si2O8 crystals. J. Non-Cryst. Solids. 534, 119948 (2020).

Article CAS Google Scholar

Maeda, K., Iwasaki, K., Urata, S., Akatsuka, K. & Yasumori, A. 3D microstructure and crack pathways of toughened CaO–Al2O3–SiO2 glass by precipitation of hexagonal CaAl2Si2O8 crystal. J. Am. Ceram. Soc. 102, 5535–5544 (2019).

Article CAS Google Scholar

Urata, S., Takato, Y. & Maeda, K. Molecular dynamics investigation of the fracture mechanism of a glass-ceramic containing cleavable crystals. J. Am. Ceram. Soc. 102, 5138–5148 (2019).

Article CAS Google Scholar

Maeda, K., Akatsuka, K. & Yasumori, A. Practical strength of damage resistant CaO–Al2O3–SiO2 glass-ceramic. Ceram. Int. 47, 8728–8731 (2021).

Article CAS Google Scholar

Kotoul, M. et al. Toughening effects quantification in glass matrix composite reinforced by alumina platelets. Acta Mater. 56, 2908–2918 (2008).

Article ADS CAS Google Scholar

Quinn, G. D. & Bradt, R. C. On the Vickers indentation fracture toughness test. J. Am. Ceram. Soc. 90, 673–680 (2007).

Article CAS Google Scholar

Marshall, D. B. et al. The compelling case for indentation as a functional exploratory and characterization tool. J. Am. Ceram. Soc. 98, 2671–2680 (2015).

Article CAS Google Scholar

Maeda, K. & Yasumori, A. Nucleation and growth of hexagonal CaAl2Si2O8 crystals in CaO–Al2O3–SiO2 glass. Mater. Lett. 206, 241–244 (2017).

Article CAS Google Scholar

Download references

The authors are deeply grateful to Kentaro Uesugi and Masayuki Uesugi for establishing the multiscale X-ray CT system and supporting our operation in this study. (The X-ray CT experiments at SPring-8 were performed with the approval of JASRI: Grant No. 2020A1603, 2020A0521). This work was supported by JSPS KAKENHI Grant No. JP19K15289.

Research Center for Structural Materials, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047, Japan

Gaku Okuma & Fumihiro Wakai

Department of Materials Science and Technology, Tokyo University of Science, 6-3-1 Niijuku, Katsushika-Ku, Tokyo, 125-8585, Japan

Kei Maeda

AGC Inc. Yokohama Technical Center, 1-1 Suehiro-cho, Tsurumi-ku, Yokohama, 230-0045, Japan

Satoshi Yoshida

Japan Synchrotron Radiation Research Institute, JASRI/SPring-8, Kouto 1-1-1, Sayo, Hyogo, 679-5198, Japan

Akihisa Takeuchi

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

G.O. designed the research together with K.M. and F.W. The sample was prepared by K.M. The experimental data were acquired by G.O., K.M., S.Y., A.T. and F.W. G.O. analyzed the data mainly. All the authors commented on the manuscript writing and the result discussion.

Correspondence to Gaku Okuma.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Video 1.

Supplementary Video 2.

Supplementary Video 3.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Okuma, G., Maeda, K., Yoshida, S. et al. Morphology of subsurface cracks in glass-ceramics induced by Vickers indentation observed by synchrotron X-ray multiscale tomography. Sci Rep 12, 6994 (2022). https://doi.org/10.1038/s41598-022-11084-0

Download citation

Received: 08 February 2022

Accepted: 11 April 2022

Published: 28 April 2022

DOI: https://doi.org/10.1038/s41598-022-11084-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

JOM (2023)

Scientific Reports (2022)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.